Effect of Various Alumina Powders on Properties of Castables
文献摘要：
To satisfy the requirements of alumina castables in specific environment and enhance their properties,alumina castables were prepared using tabular alumina,various alumina powders(07RAL,15RA,22RABL,40CA,99-20um,and 99-325mesh),and calcium aluminate cement as main raw materials,and heat treating at 110,1 000,1 600℃,respectively.Their flowability and physical properties were tested,and the morphology was researched.The results show that compared with calcined alumina and tabular alumina powders,reactive alumina has higher specific surface area and better filling performance leading to lower water demand and higher viscosity,and the castables prepared with reactive alumina have higher CCS and CMOR after heat treating at 110,1 000 and 1 600℃as well as lower PLC than those with calcined alumina and tabular alumina powders.
文献关键词：
中图分类号：
作者姓名：
SONG Yanan;WEI Guoping;CHEN Qin;SHUAI Hang;LIU Guangping;SHEN Mingke;CHEN Yaosheng;YU Yan;WANG Yulong;CAO Yaping
作者机构：
Zhejiang Zili Advanced Materials Co.,Ltd.,Shaoxing 312300,China;Zhejiang Zili High Temperature Technology Co.,Ltd.,Shaoxing 312300,China
文献出处：
引用格式：
[1]SONG Yanan;WEI Guoping;CHEN Qin;SHUAI Hang;LIU Guangping;SHEN Mingke;CHEN Yaosheng;YU Yan;WANG Yulong;CAO Yaping-.Effect of Various Alumina Powders on Properties of Castables)[J].中国耐火材料（英文版）,2022(02):45-48
A类：
Powders,Castables,castables,07RAL,15RA,22RABL,40CA,20um,325mesh
B类：
Effect,Various,Alumina,Properties,To,satisfy,requirements,specific,environment,enhance,their,properties,were,prepared,using,tabular,various,powders,calcium,aluminate,cement,main,raw,materials,heat,treating,respectively,Their,flowability,physical,tested,morphology,was,researched,results,show,that,compared,calcined,reactive,has,higher,surface,area,better,filling,performance,leading,lower,water,demand,viscosity,have,CCS,CMOR,after,well,PLC,than,those
AB值：
0.464369
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。