The Crystallization and Fracture Toughness of Transparent Glass-ceramics with Various Al2O3 Additions for Mobile Devices
文献摘要：
Li2O-Al2O3-SiO2 (LAS) glass-ceramics were prepared by a melting method. Effects of different Al2O3 content on the structure, crystallization, transmittance and fracture toughness of LAS glass-ceramics were investigated by means of XRD, FESEM and other methods as well. The results showed that the glass transition temperature and crystallization temperature of samples increased as the content of Al2O3 increased from 4.1 wt％ to 13.1 wt％, which restrained the precipitation of lithium disilicate crystals. The main crystalline phase of glass-ceramics transformed from lithium disilicate and petalite to silicon dioxide, which reduced the fracture toughness of glass-ceramics. When the Al2O3 content was 7.1 wt％, the specimen had outstanding transmittance and fracture toughness. The transmittance was 90.32％. The fracture toughness was 1.13 MPa ? m1/2. Compared with high-alumina glass, the fracture toughness of the glass-ceramic was greatly improved, and it could be used as a new type of protective material for mobile devices.
文献关键词：
中图分类号：
作者姓名：
ZHENG Weihong;LI Changqin;YUAN Jian;TIAN Peijing;TENG Fei;WANG Weizheng;PENG Zhigang;WANG Wei
作者机构：
State Key Laboratory of Silicate Building Materials,Wuhan University of Technology,Wuhan 430070,China;Shahe Research Institute of Glass Technology,Shahe 054100,China;School of Automotive Engineering,Wuhan University of Technology,Wuhan 430070,China;Hubei Key Laboratory of Advanced Technology for Automotive Components,Wuhan University of Technology,Wuhan 430070,China;Hu-bei Collaborative Innovation Center for Automotive Components Technology,Wuhan University of Technology,Wuhan 430070,China
文献出处：
引用格式：
[1]ZHENG Weihong;LI Changqin;YUAN Jian;TIAN Peijing;TENG Fei;WANG Weizheng;PENG Zhigang;WANG Wei-.The Crystallization and Fracture Toughness of Transparent Glass-ceramics with Various Al2O3 Additions for Mobile Devices)[J].武汉理工大学学报（材料科学版）（英文版）,2022(03):378-384
A类：
disilicate,petalite
B类：
Crystallization,Fracture,Toughness,Transparent,Glass,ceramics,Various,Al2O3,Additions,Mobile,Devices,Li2O,SiO2,LAS,glass,were,prepared,by,melting,Effects,different,content,structure,crystallization,transmittance,fracture,toughness,investigated,means,FESEM,other,methods,well,results,showed,that,transition,temperature,samples,increased,from,wt,which,restrained,precipitation,lithium,crystals,main,crystalline,phase,transformed,silicon,dioxide,reduced,When,was,specimen,had,outstanding,m1,Compared,high,alumina,greatly,improved,could,be,used,new,type,protective,material,mobile,devices