Effect of Reduction Temperature on the Hydrodesulfurization Performance of Carbon-doped Alumina-supported Nickel Phosphide Catalyst
文献摘要：
Nickel phosphide–carbon-doped alumina (Ni2P/Al2O3–C) catalysts with 10 wt.％ Ni2P loading were successfully prepared via a hydrothermal reduction process and the effect of reduction temperature on the hydrodesulfurization (HDS) performance of the as-prepared Ni2P/Al2O3–C catalysts was investigated. The properties of the support (Al2O3–C) and Ni2P/Al2O3–C catalysts were characterized by transmission electron microscopy, scanning electron microscopy, Brunauer–Emmett–Teller measurements, X-ray diffractometry, and X-ray photoelectron spectroscopy. The results indicated that the incorporation of carbon in the support aided the reduction of Ni2P. With an increase in the reduction temperature, Ni and Ni12P5 were first generated and then converted into crystalline Ni2P. Furthermore, a higher reduction temperature enhanced the HDS performance of the catalyst by generating more well-dispersed active-phase crystalline Ni2P.
文献关键词：
中图分类号：
作者姓名：
Jiang Nan;Wang Shuai;Jiang Bolong
作者机构：
Innovation Institute for Sustainable Maritime Architecture Research and Technology,Qingdao University of Technology,Qingdao,266000,China;Provincial Key Laboratory of Oil&Gas Chemical Technology,College of Chemistry&Chemical Engineering,Northeast Petroleum University,Daqing,163318,China
文献出处：
引用格式：
[1]Jiang Nan;Wang Shuai;Jiang Bolong-.Effect of Reduction Temperature on the Hydrodesulfurization Performance of Carbon-doped Alumina-supported Nickel Phosphide Catalyst)[J].中国炼油与石油化工（英文版）,2022(03):44-51
A类：
Hydrodesulfurization,Phosphide,Ni12P5
B类：
Effect,Reduction,Temperature,Performance,Carbon,doped,Alumina,supported,Nickel,Catalyst,phosphide,carbon,alumina,Ni2P,Al2O3,catalysts,wt,loading,were,successfully,prepared,via,hydrothermal,reduction,process,effect,temperature,hydrodesulfurization,HDS,performance,was,investigated,properties,characterized,by,transmission,microscopy,scanning,Brunauer,Emmett,Teller,measurements,ray,diffractometry,photoelectron,spectroscopy,results,indicated,that,incorporation,aided,With,increase,first,generated,then,converted,into,crystalline,Furthermore,higher,enhanced,generating,well,dispersed,active,phase
AB值：
0.547681
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。