Optimization of cold spray additive manufactured AA2024/Al2O3 metal matrix composite with heat treatment

文献摘要：

In this study,the effects of annealing and solution aging heat treatment on the microstructure and me-chanical properties of cold spray additive manufactured(CSAMed)AA2024/Al2O3 composite were inves-tigated.The results showed that both annealing and solution aging enhanced the interfacial bonding be-tween the deposited AA2024 particles in the composite.The tensile properties of CSAMed AA2024/Al203 composite were significantly improved by 13.8％for ultimate tensile strength and 47.8％for elongation af-ter solution aging.Microstructural examination and fractographic analysis showed that the fracture mech-anism between the adjacent AA2024 particles changed from brittle to ductile-dominant mode after heat treatment.However,the interfacial bonding between the AA2024 and A1203 particles cannot be improved.For the improvement of mechanical properties,the solution aging was slightly better than annealing.In addition,low-temperature annealing greatly reduced the anisotropy of the mechanical properties of CSAMed AA2024/Al203 composite.

文献关键词：

中图分类号：

[1] 医药、卫生（R） / 基础医学（R3） / 病理学（R36） / 病理过程（R364）

[2] 医药、卫生（R） / 神经病学与精神病学（R74） / 神经病学（R741）

[3] 医药、卫生（R） / 临床医学（R4） / 治疗学（R45） / 生物疗法（R456）

作者姓名：

Dong Wu;Wenya Li;Kun Liu;Yang Yang;Sijie Hao

作者机构：

State Key Laboratory of Solidification Processing,Shaanxi Key Laboratory of Friction Welding Technologies,Northwestern Polytechnical University,Xi'an 710072,China

文献出处：

材料科学技术（英文版）

引用格式：

[1]Dong Wu;Wenya Li;Kun Liu;Yang Yang;Sijie Hao-.Optimization of cold spray additive manufactured AA2024/Al2O3 metal matrix composite with heat treatment)[J].材料科学技术（英文版）,2022(11):211-224

A类：

CSAMed,fractographic

B类：

Optimization,cold,spray,additive,manufactured,AA2024,Al2O3,metal,matrix,composite,heat,treatment,In,this,study,effects,annealing,solution,aging,microstructure,properties,were,inves,tigated,results,showed,that,both,enhanced,interfacial,bonding,deposited,particles,tensile,Al203,significantly,improved,by,ultimate,strength,elongation,Microstructural,examination,analysis,fracture,anism,between,adjacent,changed,from,brittle,ductile,dominant,mode,after,However,A1203,cannot,For,improvement,mechanical,was,slightly,better,than,addition,low,temperature,greatly,reduced,anisotropy

AB值：

0.465515

相似文献

Effects of multipass friction stir processing and Mg addition on the microstructure and tensile properties of Al 1050 alloys

Shahin Arshadi Rastabi;Masoud Mosallaee-Department of Mining and Metallurgy, Yazd University, Yazd, Iran

Compressive fatigue behavior and failure evolution of additive fiber-reinforced cemented tailings composites

Jiajian Li;Shuai Cao;Erol Yilmaz;Yunpeng Liu-School of Civil and Resources Engineering,University of Science and Technology Beijing,Beijing 100083,China;State Key Laboratory of High-Efficient Mining and Safety of Metal Mines of Ministry of Education,University of Science and Technology Beijing,Beijing 100083,China;Department of Civil Engineering,Geotechnical Division,Recep Tayyip Erdogan University,Fener,Rize TR53100,Turkey;State Key Laboratory of Silicate Materials for Architectures(Wuhan University of Technology),Wuhan 430070,China

Microstructure and mechanical properties of friction pull plug welding for 2219-T87 aluminum alloy with tungsten inert gas weld

Zhen Shao;Lei Cui;Lijun Yang;Peng Lu;Huimiao Wang;Zhuanping Sun;Jianling Song-Tianjin Key Laboratory of Advanced Joining Technology,School of Materials Science and Engineering,Tianjin University,Tianjin 300350,China;Tianjin Space Launch Vehicle Manufacturing Co.Ltd,Tianjin 300457,China

Effects of Li addition on the microstructure and tensile properties of the extruded Mg–1Zn–xLi alloy

Jun Zhao;Bin Jiang;Qinghang Wang;Ming Yuan;Yanfu Chai;Guangsheng Huang;Fusheng Pan-School of Mechanical and Electrical Engineering,Hunan City University,Yiyang 413002,China;State Key Laboratory of Mechanical Transmissions,College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China;School of Mechanical Engineering,Yangzhou University,Yangzhou 225127,China;School of Mechanical and Electrical Engineering,Shaoxing University,Shaoxing 312000,China

Influence of process parameters and aging treatment on the microstructure and mechanical properties of AlSi8Mg3 alloy fabricated by selectivelaser melting