Effect of modifying matrix microstructures and nanosized precipitates on strengthening mechanisms and ductile-to-brittle-transition-temperature in a 1000 MPa Ni-Cr-Mo-Cu steel
文献摘要:
A superior combination of yield strength(1001 MPa)and-20℃impact toughness(166 J)was obtained in Nb-V-Ti-microalloyed Ni-Cr-Mo-Cu steel treated by direct quenching and tempering route(DQT).The tested steels treated by DQT route and re-austenitization and tempering route(QT)were compared with each other in terms of mechanical properties and microstructures characterized by optical microscopy,transmission electron microscopy,X-ray diffraction,electron back-scattered diffraction method and so on.Strength and Vickers hardness of the tested steel treated by the above two routes vary with isothermal aging temperature(400-600℃),shown as under-aged state,peak-aged state and over-aged state.All DQT specimens show higher strength and Vickers hardness than QT specimens with the same aging condition.Furthermore,the largest difference of yield strength between DQT and QT specimens was shown in DQT600 and QT600 specimens.DQT60 or QT600 specimens refers to direct quenched(DQ)or quenched(Q)specimens isothermally aged at 600℃.The main disparities in quenched microstructure between DQ and Q specimens are mainly in morphology of prior austenite grains,dislocation density of martensite matrix and solution amount of Nb and Mo elements dissolving in martensite matrix,which play key roles in affecting microstructure and mechanical properties of DQT and QT specimens.Higher dislocation density of matrix and finer average diameter of both MC(M is any combination of Nb,Mo and V)and Cu-rich particles were shown in DQT6000 specimens than in QT600 specimens.Strengthening from dislocations and nanosized MC and Cu-rich particles mainly leads to the largest difference of yield strength between DQT600 and QT600 specimens.In addition,strong dislocation strengthening and precipitation strengthening in DQT600 specimen also elevated its ductile-to-brittle-transition-temperature,compared with QT600 specimen.
文献关键词:
作者姓名:
Fei Zhu;Li Yang;Feng Chai;Xiao-bing Luo;Cai-fu Yang;Zheng-yan Zhang
作者机构:
Department of Structural Steels,Central Iron and Steel Research Institute,Beijing 100081,China;Material Digital R&D Center,China Iron and Steel Research Institute Group,Beijing 100081,China
引用格式:
[1]Fei Zhu;Li Yang;Feng Chai;Xiao-bing Luo;Cai-fu Yang;Zheng-yan Zhang-.Effect of modifying matrix microstructures and nanosized precipitates on strengthening mechanisms and ductile-to-brittle-transition-temperature in a 1000 MPa Ni-Cr-Mo-Cu steel)[J].钢铁研究学报(英文版),2022(08):1257-1276
A类:
microalloyed,austenitization,DQT600,DQT60,DQT6000
B类:
Effect,modifying,matrix,microstructures,nanosized,precipitates,strengthening,mechanisms,ductile,brittle,transition,temperature,Mo,superior,combination,yield,impact,toughness,was,obtained,Nb,Ti,treated,by,direct,quenching,tempering,tested,steels,were,compared,each,terms,mechanical,properties,characterized,optical,microscopy,transmission,electron,ray,diffraction,back,scattered,method,Vickers,hardness,above,two,routes,vary,aging,shown,under,aged,state,peak,over,All,specimens,higher,than,same,condition,Furthermore,largest,difference,between,refers,quenched,isothermally,disparities,mainly,morphology,prior,austenite,grains,density,martensite,solution,amount,elements,dissolving,which,play,key,roles,affecting,Higher,finer,average,diameter,both,MC,any,rich,particles,Strengthening,from,dislocations,leads,In,addition,strong,precipitation,also,elevated,its
AB值:
0.389767
相似文献
In situ neutron diffraction unravels deformation mechanisms of a strong and ductile FeCrNi medium entropy alloy
L.Tang;F.Q.Jiang;J.S.Wróbel;B.Liu;S.Kabra;R.X.Duan;J.H.Luan;Z.B.Jiao;M.M.Attallah;D.Nguyen-Manh;B.Cai-School of Metallurgy and Materials,University of Birmingham,B15 2TT,United Kingdom;Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;Faculty of Materials Science and Engineering,Warsaw University of Technology,ul.Wo?oska 141,Warsaw 02-507,Poland;State Key Laboratory for Powder Metallurgy,Central South University,Changsha 410083,China;Rutherford Appleton Laboratory,ISIS Facility,Didcot OX11 0QX,United Kingdom;Department of Materials Science and Engineering,City University of Hong Kong,Kowloon,Hong Kong,China;Department of Mechanical Engineering,The Hong Kong Polytechnic University,Hung Hom,Hong Kong,China;CCFE,United Kingdom Atomic Energy Authority,Abingdon,Oxfordshire OX14 3DB,United Kingdom
γ"variant-sensitive deformation behaviour of Inconel 718 superalloy
R.Y.Zhang;H.L.Qin;Z.N.Bi;Y.T.Tang;J.Araújo de Oliveira;T.L.Lee;C.Panwisawas;S.Y.Zhang;J.Zhang;J.Li;H.B.Dong-Centre of Excellence for Advanced Materials,Dongguan 523808,China;School of Engineering,University of Leicester,University Road,Leicester LEI 7RH,United Kingdom;Beijing Key Laboratory of Advanced High Temperature Materials,Central Iron and Steel Research Institute,Beijing 100081,China;Department of Materials,University of Oxford,Parks Road,Oxford OX1 3PH,United Kingdom;StressMap,Engineering and Innovation Department,The Open University,Walton Hall,Milton Keynes MK7 6AA,United Kingdom;ISIS Neutron Source,Rutherford Appleton Laboratory,Harwell Science and Innovation Campus,Chilton,Oxfordshire OX11 OQX,United Kingdom;School of Material Science and Engineering,Shanghai Jiao Tong University,Shanghai 200240,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。