Effect of strain rate on fracture behaviour of Cr18Ni11Ti stainless steel at high temperatures
文献摘要：
The effect of strain rate on the fracture behaviour of Cr18Ni11Ti stainless steel at high temperatures was analysed.The steel was subjected to solid solution treatment at 1050℃and ageing at 650℃for 24 h.The high-temperature tensile properties of Cr18Ni11Ti stainless steel were subsequently investigated via high-temperature tensile testing at 650℃and different strain rates(1.43×10-1,1.43×10-2,1.43×10-3,1.43×10-4,and 1.43×10-5 s-1).The microstructure,precipitated phase,tensile fracture surface,and dislocation of the experimental steel were analysed by scanning electron microscopy,transmission electron microscopy and energy spectrometry.The results show that Cr18Ni11Ti stainless steel is mainly austenite,with a large number of twin crystals,chromium-rich precipitated phase and composite precipitated phases of TiC and AlMgCaO.With decreases in strain rate,the yield strength,ultimate tensile strength,and reduction in area also decrease.When the strain rate is high,obvious necking and ductile fracture occur in the experimental steel.However,when the strain rate is reduced to 1.43×10-5 s-1,the necking phenomenon is not obvious and intergranular brittle fracture appears.Greater segregation of P and S contents at grain boundaries,or dislocation motion creep and grain-boundary sliding creep,leads to brittle fracture of the steel at lower strain rates of 1.43×10-4 to 1.43×10-5 s-1.
文献关键词：
中图分类号：
作者姓名：
Xin-li Song;Chang-hu Huang;Juan Jia;Jing Liu
作者机构：
The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology,Wuhan 430081,Hubei,China;Hubei Engineering Technology Research Center of Marine Materials and Service Safety,Wuhan 430081,Hubei,China
文献出处：
引用格式：
[1]Xin-li Song;Chang-hu Huang;Juan Jia;Jing Liu-.Effect of strain rate on fracture behaviour of Cr18Ni11Ti stainless steel at high temperatures)[J].钢铁研究学报（英文版）,2022(06):1004-1011
A类：
Cr18Ni11Ti,AlMgCaO
B类：
Effect,strain,fracture,behaviour,stainless,steel,high,temperatures,effect,was,analysed,subjected,solid,solution,treatment,ageing,tensile,properties,were,subsequently,investigated,via,testing,different,rates,microstructure,precipitated,surface,dislocation,experimental,by,scanning,electron,microscopy,transmission,energy,spectrometry,results,show,that,mainly,austenite,large,number,twin,crystals,chromium,rich,composite,phases,TiC,With,decreases,yield,strength,ultimate,reduction,area,also,When,obvious,necking,ductile,occur,However,when,reduced,phenomenon,not,intergranular,brittle,appears,Greater,segregation,contents,grain,boundaries,motion,creep,boundary,sliding,leads,lower
AB值：
0.467944
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。