Effect of spark plasma sintering and reinforcements on the formation of ultra-fine and nanograins in AA2024-TiB2-Y hybrid composites
文献摘要：
This study reports the influence of sintering mechanism and reinforcement materials on the formation of ultra-fine and nanograins in Al-TiB2-Y nanohybrid composites.The mechanical properties of the composites and their corresponding micro and nanostructures are correlated.The experimental and characterization results revealed that despite the addition of TiB2,the hard and brittle Al3Ti phase formation in the composites was suppressed and hence,their ductility was retained.It was found that yttrium content of 0.3 wt％was the optimum amount which created advantageous spark plasma sintering conditions,and the addition of 0.3 wt％promoted the formation of bi-modal size grains(ultra-fine and nano)along with micro grains,Ω and other nano precipitates,resulting in a significant enhancement in the composite properties.The formation of ultra-fine and nanograins may be attrib-uted to the combined effect of melting and rapid solidification at necking zones due to Joule's heating and thermo-mechanical fatigue.Among all the sintered composites,the highest hardness(137 HV),ultimate tensile strength(UTS)(496 MPa),yield strength(YS)(438 MPa)with 15.7％elongation were obtained in the sintered sample reinforced with 1.0 wt％TiB2 and 0.3 wt％yttrium.
文献关键词：
中图分类号：
作者姓名：
CH.Suresh Vidyasagar;D.B.Karunakar
作者机构：
Department of Architecture and Planning,Indian Institute of Technology Roorkee,247667,India;Mechanical and Industrial Engineering Department,Indian Institute of Technology Roorkee,247667,India
文献出处：
引用格式：
[1]CH.Suresh Vidyasagar;D.B.Karunakar-.Effect of spark plasma sintering and reinforcements on the formation of ultra-fine and nanograins in AA2024-TiB2-Y hybrid composites)[J].自然科学进展·国际材料（英文）,2022(01):79-86
A类：
B类：
Effect,spark,plasma,sintering,reinforcements,formation,ultra,fine,nanograins,AA2024,TiB2,composites,This,study,reports,influence,mechanism,materials,nanohybrid,mechanical,properties,their,corresponding,micro,nanostructures,are,correlated,experimental,characterization,results,revealed,that,despite,addition,brittle,Al3Ti,phase,was,suppressed,hence,ductility,retained,It,found,yttrium,content,wt,optimum,amount,which,created,advantageous,conditions,promoted,modal,size,along,other,precipitates,resulting,significant,enhancement,may,be,attrib,uted,combined,effect,melting,rapid,solidification,necking,zones,due,Joule,heating,thermo,fatigue,Among,all,sintered,highest,hardness,HV,ultimate,tensile,strength,UTS,yield,YS,elongation,were,obtained,sample,reinforced
AB值：
0.569974
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。