Enhanced tribological properties of aligned graphene-epoxy composites
文献摘要:
The random distribution of graphene in epoxy matrix hinders the further applications of graphene-epoxy composites in the field of tribology.Hence,in order to fully utilize the anisotropic properties of graphene,highly aligned graphene-epoxy composites(AGEC)with horizontally oriented structure have been fabricated via an improved vacuum filtration freeze-drying method.The frictional tests results indicated that the wear rate of AGEC slowly increased from 5.19×10-6 mm3/(N·m)to 2.87×10-5 mm3/(N·m)with the increasing of the normal load from 2 to 10 N,whereas the friction coefficient(COF)remained a constant of 0.109.Compared to the neat epoxy and random graphene-epoxy composites(RGEC),the COF of AGEC was reduced by 87.5%and 71.2%,and the reduction of wear rate was 86.6%and 85.4%at most,respectively.Scanning electron microscope(SEM)observations illustrated that a compact graphene self-lubricant film was formed on the worn surface of AGEC,which enables AGEC to possess excellent tribological performance.Finally,in light of the excellent tribological properties of AGEC,this study highlights a pathway to expand the tribological applications of graphene-epoxy composites.
文献关键词:
作者姓名:
Yuefeng DU;Zhenyu ZHANG;Dong WANG;Lezhen ZHANG;Junfeng CUI;Yapeng CHEN;Mingliang WU;Ruiyang KANG;Yunxiang LU;Jinhong YU;Nan JIANG
作者机构:
Key Laboratory for Precision and Non-Traditional Machining Technology of Ministry of Education,Dalian University of Technology,Dalian 116024,China;Beijing Spacecrafts Manufacturing Factory Co.,Ltd.,China Academy of Space Technology,Beijing 100094,China;Weichai Power Co.,Ltd.,Weifang 261061,China;Key Laboratory of Marine Materials and Related Technologies,Zhejiang Key Laboratory of Marine Materials and Protective Technologies,Ningbo Institute of Materials Technology and Engineering(NIMTE),Chinese Academy of Sciences,Ningbo 315201,China
文献出处:
引用格式:
[1]Yuefeng DU;Zhenyu ZHANG;Dong WANG;Lezhen ZHANG;Junfeng CUI;Yapeng CHEN;Mingliang WU;Ruiyang KANG;Yunxiang LU;Jinhong YU;Nan JIANG-.Enhanced tribological properties of aligned graphene-epoxy composites)[J].摩擦(英文),2022(06):854-865
A类:
AGEC,RGEC
B类:
Enhanced,tribological,properties,aligned,graphene,epoxy,composites,random,distribution,matrix,hinders,further,applications,field,tribology,Hence,order,fully,utilize,anisotropic,highly,horizontally,oriented,structure,have,been,fabricated,via,improved,vacuum,filtration,freeze,drying,method,frictional,tests,results,indicated,that,wear,slowly,increased,from,mm3,increasing,normal,load,whereas,coefficient,COF,remained,constant,Compared,neat,was,reduced,by,reduction,most,respectively,Scanning,electron,microscope,observations,illustrated,compact,self,lubricant,film,formed,worn,surface,which,enables,possess,excellent,performance,Finally,this,study,highlights,pathway,expand
AB值:
0.520877
相似文献
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。