An innovative process of clad teeming for preparing slab ingot
文献摘要：
An innovative process of clad teeming was proposed to prepare slab ingot,which featured a built-in cold core to inhibit solidification defects.A 20-kg clad ingot was prepared in the experiment,using a volume ratio of solid core to molten steel of 1∶13 and a preheating temperature of cold core of 573 K.Solidification microstructures of the clad ingot were analyzed by comparing with a reference ingot without cold core.Interfacial morphologies and mechanical properties of the clad ingot were studied before and after hot rolling.The effect of cold core on heat transfer and nucleation during the solidification in clad ingot was analyzed.Results show that the solidification microstructures in the clad ingot are refined and homogenized obviously.The grain size in the center of the reference ingot is 2-3 times greater than that of clad ingot,and there is almost no columnar grain in the clad ingot.The interfacial shear strength reaches 318 Mpa,which shows excellent metallurgical bonding at the interface of cold core and molten steel.Tiny defects at the interface are eliminated,and interfacial shear strength reaches 426 Mpa after hot rolling with a 68.4％total reduction ratio.The experiment and analysis of this process are expected to provide a new idea to prepare large ingots with refinement and homogeneity at a low cost.
文献关键词：
中图分类号：
作者姓名：
Wen-bin Ma;Yao-hui Jin;Yu-an Jing;Wen-bin Li;Wei-da Yu;Guang-long Li;Wan-ming Li
作者机构：
School of Materials and Metallurgy,University of Science and Technology Liaoning,Anshan 114051,Liaoning,China;Iron and Steel Research Institutes of Ansteel Group Corporation,Anshan 114001,Liaoning,China
文献出处：
引用格式：
[1]Wen-bin Ma;Yao-hui Jin;Yu-an Jing;Wen-bin Li;Wei-da Yu;Guang-long Li;Wan-ming Li-.An innovative process of clad teeming for preparing slab ingot)[J].钢铁研究学报（英文版）,2022(12):2006-2015
A类：
teeming
B类：
An,innovative,process,clad,preparing,slab,was,proposed,which,featured,built,cold,core,inhibit,solidification,defects,prepared,experiment,using,volume,ratio,molten,steel,preheating,temperature,Solidification,microstructures,were,analyzed,by,comparing,reference,without,Interfacial,morphologies,mechanical,properties,studied,before,after,hot,rolling,effect,transfer,nucleation,during,Results,that,refined,homogenized,obviously,grain,size,center,times,greater,than,there,almost,columnar,interfacial,shear,strength,reaches,Mpa,shows,excellent,metallurgical,bonding,interface,Tiny,eliminated,total,reduction,analysis,this,expected,provide,new,idea,large,ingots,refinement,homogeneity,low,cost
AB值：
0.444903
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。