Interfacial bonding characteristics and mechanical properties of H68/AZ31B clad plate
文献摘要：
Interfacial bonding, microstructures, and mechanical properties of an explosively-welded H68/AZ31B clad plate were systematic-ally studied. According to the results, the bonding interface demonstrated a "wavy-like" structure containing three typical zones/layers: (1) dif-fusion layer adjacent to the H68 brass plate; (2) solidification layer of melted metals at the interface; (3) a layer at the side of AZ31B alloy that experienced severe deformation. Mixed copper, CuZn2, and α-Mg phases were observed in the melted-solidification layer. Regular polygonal grains with twins were found at the H68 alloy side, while fine equiaxed grains were found at the AZ31B alloy side near the interface due to re-crystallization. Nanoindentation results revealed the formation of brittle intermetallic CuZn2 phases at the bonding interface. The interface was bonded well through metallurgical reactions due to diffusion of Cu, Zn, and Mg atoms across the interface and metallurgic reaction of partially melted H68 and AZ31B alloys.
文献关键词：
中图分类号：
作者姓名：
Tingting Zhang;Wenxian Wang;Jie Zhang;Zhifeng Yan
作者机构：
Advanced Forming and Intelligent Equipment Research Institute,Taiyuan University of Technology,Taiyuan 030024,China;College of Mechanical and Vehicle Engineering,Taiyuan University of Technology,Taiyuan 030024,China;College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China;Key Laboratory of Interface Science and Engineering in Advanced Materials,Ministry of Education,Taiyuan 030024,China;Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan 030024, China
文献出处：
引用格式：
[1]Tingting Zhang;Wenxian Wang;Jie Zhang;Zhifeng Yan-.Interfacial bonding characteristics and mechanical properties of H68/AZ31B clad plate)[J].矿物冶金与材料学报,2022(06):1237-1248
A类：
H68,CuZn2,metallurgic
B类：
Interfacial,bonding,characteristics,mechanical,properties,AZ31B,clad,plate,microstructures,explosively,welded,were,systematic,studied,According,results,interface,demonstrated,wavy,like,containing,three,typical,zones,layers,adjacent,brass,solidification,melted,metals,side,that,experienced,severe,deformation,Mixed,copper,Mg,phases,observed,Regular,polygonal,grains,twins,found,while,fine,equiaxed,near,due,crystallization,Nanoindentation,revealed,brittle,intermetallic,was,bonded,well,through,metallurgical,reactions,diffusion,atoms,across,partially,alloys
AB值：
0.466049
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。