Structures and macrosegregation of a 2024 aluminum alloy fabricated by direct chill casting with double cooling field
文献摘要：
Central region coarse grains and centerline segregation are common defects in aluminum ingots fabricated by direct chill (DC) casting. A double cooling field was introduced into the DC casting process to reduce these defects, whereby the external cooling was supplied by the mold and water jets, and intercooling was achieved by inserting a rod of the same alloy into the molten pool along the central axis of the ingot. Rather than forming a good metallurgical interface during solid-liquid compound casting, in the present work, the purpose of inserting the rod is to enforce internal cooling and consequently decrease the sump depth. Moreover, the insertion provides more nucleation sites with the unmolten α-Al particles. The structure and the macrosegregation of 2024 Al alloy ingots prepared by DC casting with and without the inserts were investigated. Results show that when the inserting position is 50 mm above the upper edge of the graphite ring, significant grain refinement in the central region of the ingot and a reduced centerline segregation are achieved.
文献关键词：
中图分类号：
作者姓名：
Cheng Zhu;Zhi-hao Zhao;Qing-feng Zhu;Gao-song Wang;Yu-bo Zuo;Gao-wu Qin
作者机构：
Research Center for Metallic Wires,School of Materials Science and Engineering,Northeastern University,Shenyang 110819,China;Key Laboratory of Electromagnetic Processing of Materials,Ministry of Education,Northeastern University,Shenyang 110819,China;Key Laboratory of Anisotropy and Texture of Materials,Ministry of Education,Northeastern University,Shenyang 110819,China
文献出处：
引用格式：
[1]Cheng Zhu;Zhi-hao Zhao;Qing-feng Zhu;Gao-song Wang;Yu-bo Zuo;Gao-wu Qin-.Structures and macrosegregation of a 2024 aluminum alloy fabricated by direct chill casting with double cooling field)[J].中国铸造,2022(01):1-8
A类：
macrosegregation,intercooling,unmolten
B类：
Structures,aluminum,alloy,fabricated,direct,chill,casting,double,field,Central,region,coarse,grains,centerline,common,defects,ingots,DC,was,introduced,into,process,these,whereby,external,supplied,mold,water,jets,achieved,inserting,same,pool,along,central,axis,Rather,than,forming,good,metallurgical,interface,during,solid,liquid,compound,present,work,purpose,enforce,internal,consequently,decrease,sump,depth,Moreover,insertion,provides,more,nucleation,sites,particles,structure,prepared,without,inserts,were,investigated,Results,show,that,when,position,above,upper,edge,graphite,significant,refinement,reduced