Effect of dimensionless heat input during laser solid forming of high-strength steel
文献摘要：
Laser solid forming(LSF)technology can be used to rapidly manufacture and repair high-strength steel parts with superior performance,but the value of the heat input during operation is difficult to quantify,which has a substantial impact on the microstructure and mechanical properties of the parts.A promis-ing method to improve the forming efficiency and quality of LSFed parts is to accurately control the heat input and explore its relationship with the microstructure and mechanical properties.To remove the interference of other variables from the experiment,the dimensionless heat input Q* was introduced.The Q* values were designed in advance to calculate the experimental parameters used to perform the LSF experiment.The microstructure was observed at different regions of the sample,and its mechanical properties were analyzed.From the results,the following conclusions were drawn.The Q* value was di-rectly related to the cooling rate and heat accumulation in the top structure,leading to the formation of different microstructures;it also modified the original structure at the bottom,affecting the subsequent thermal cycle and indirectly changing the tempered martensite morphology.The heat input also affected the mechanical properties of the sample.The hardness of the stable zone decreased with increasing Q*value,and the lowest value was 190 HV.Similarly,the tensile strength and yield strength of the LSFed samples decreased considerably with increasing Q* value,and the lowest values were 735 and 604 MPa,respectively.Only the elongation and reduction in the area increased after a slight decrease.The Q* value had a significant effect on heat treatment.When Q*=2.9,the increase in tensile strength and yield strength after heat treatment was the largest(29％and 44％,respectively).
文献关键词：
中图分类号：
作者姓名：
Chunping Huang;Renyu Liang;Fenggang Liu;Haiou Yang;Xin Lin
作者机构：
National Defense Key Discipline Laboratory of Light Alloy Processing Science and Technology,Nanchang Hangkong University,Nanchang 330063,China;Key Laboratory of Metal High Performance Additive Manufacturing and Innovative Design,MIIT China,Northwestern Polytechnical University,Xi'an 710072,China
文献出处：
引用格式：
[1]Chunping Huang;Renyu Liang;Fenggang Liu;Haiou Yang;Xin Lin-.Effect of dimensionless heat input during laser solid forming of high-strength steel)[J].材料科学技术（英文版）,2022(04):127-137
A类：
LSFed
B类：
Effect,dimensionless,heat,input,during,laser,solid,forming,high,strength,steel,Laser,technology,be,used,rapidly,manufacture,repair,parts,superior,performance,but,operation,difficult,quantify,which,has,substantial,impact,mechanical,properties,promis,method,improve,efficiency,quality,accurately,control,explore,its,relationship,To,remove,interference,other,variables,from,was,introduced,values,were,designed,advance,calculate,experimental,parameters,observed,different,regions,analyzed,From,results,following,conclusions,drawn,related,cooling,accumulation,top,leading,formation,microstructures,also,modified,original,bottom,affecting,subsequent,thermal,cycle,indirectly,changing,tempered,martensite,morphology,affected,hardness,stable,zone,decreased,increasing,lowest,HV,Similarly,tensile,yield,samples,considerably,respectively,Only,elongation,reduction,area,increased,after,slight,had,significant,effect,treatment,When,largest
AB值：
0.47754
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。