Effect of titanium microalloying on microstructure and mechanical properties of vanadium microalloyed steels for hot forging
文献摘要：
Effect of titanium microalloying on the microstructure and mechanical properties of vanadium microalloyed steels for hot forging was studied.Titanium microalloying improves the mechanical properties mainly through refining the austenite grains.When the heating temperature is in the range of 1050-1300℃,the austenite grain diameter is decreased from 77-133 to 26-68 pm by titanium microalloying.With the decrease in austenite grain diameter,the final microstructure is refined significantly,and the high misorientation boundaries are increased.After the steel is heated at 1200℃(the common hot forging temperature)and cooled slowly,titanium microalloying decreases the yield strength from 548.4 to 519.4 MPa,and the tensile strength decreases from 842.7 to 808.7 MPa.However,the elongation increases from 19.0％to 21.4％,and the impact energy increases from 9.8 to 38.2 J.V-Ti steel has a better combination of strength,plasticity and toughness than V steel.In addition,the nucleation of intragranular ferrite idiomorphs is promoted by titanium microal-loying,which may have a beneficial effect on the property of steels with coarse microstructure caused by the critical deformation in hot die forging.
文献关键词：
中图分类号：
作者姓名：
Fan Zhao;Guo-ning He;Ya-zheng Liu;Zhi-hao Zhang;Jian-xin Xie
作者机构：
Beijing Laboratory of Metallic Materials and Processing for Modern Transportation,Institute for Advanced Materials and Technology,University of Science and Technology Beijing,Beijing 100083,China;State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology,Wuhan 430074,Hubei,China;School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China
文献出处：
引用格式：
[1]Fan Zhao;Guo-ning He;Ya-zheng Liu;Zhi-hao Zhang;Jian-xin Xie-.Effect of titanium microalloying on microstructure and mechanical properties of vanadium microalloyed steels for hot forging)[J].钢铁研究学报（英文版）,2022(02):295-306
A类：
microalloyed,idiomorphs,microal,loying
B类：
Effect,titanium,microalloying,microstructure,mechanical,properties,vanadium,steels,hot,forging,was,studied,Titanium,improves,mainly,through,refining,austenite,grains,When,heating,temperature,range,diameter,decreased,from,pm,by,With,final,refined,significantly,high,misorientation,boundaries,are,increased,After,heated,common,cooled,slowly,decreases,yield,strength,tensile,However,elongation,increases,impact,energy,has,better,combination,plasticity,toughness,than,In,addition,nucleation,intragranular,ferrite,promoted,which,may,have,beneficial,effect,property,coarse,caused,critical,deformation
AB值：
0.45493
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。