Dependence of mechanical behavior on grain size of metastable Ti-Nb-O titanium alloy
文献摘要:
Cold-rolled metastable β-type Ti-38Nb-0.2O alloy was subjected to annealing treatment to obtain different pre-cipitates and grain sizes.The influence of annealing on microstructure and mechanical properties was investi-gated.The alloy annealed at 673 K or 773 K exhibited a single-stage yielding with high strength and low uniform elongation,due to the residual work hardening and the precipitation of ω or α phases.The alloy annealed at above 873 K exhibited an obvious double yielding behavior resulting from the stress-induced martensitic trans-formation.The grain growth kinetics of single β phase alloy is sensitive to temperature,and it is suggested that the existence of oxygen decreases the grain growth exponent and increases the required activation energy for grain growth.The critical stress for slip decreased monotonously with the increase of grain size,following the classic Hall-Petch relationship.However,the critical stress for martensitic transformation decreased to a minimum and then increased again,as the grain size increased.The results are worth for design of the heat-treatment parameters of the Ti-38Nb-0.2O alloy for engineering applications.
文献关键词:
作者姓名:
Junshuai Wang;Wenlong Xiao;Yu Fu;Lei Ren;Chaoli Ma
作者机构:
Key Laboratory of Aerospace Advanced Materials and Performance of Ministry of Education,School of Materials Science and Engineering Beihang University,Beijing,100191,China;Yunnan Innovation Institute of Beihang University,Kunming Yunnan,650000,China
引用格式:
[1]Junshuai Wang;Wenlong Xiao;Yu Fu;Lei Ren;Chaoli Ma-.Dependence of mechanical behavior on grain size of metastable Ti-Nb-O titanium alloy)[J].自然科学进展·国际材料(英文),2022(01):63-71
A类:
38Nb,cipitates
B类:
Dependence,mechanical,behavior,grain,metastable,Ti,titanium,alloy,Cold,rolled,type,2O,was,subjected,annealing,treatment,obtain,different,sizes,influence,microstructure,properties,investi,gated,annealed,exhibited,single,stage,yielding,high,strength,uniform,elongation,due,residual,work,hardening,precipitation,phases,above,obvious,double,resulting,from,stress,induced,martensitic,growth,kinetics,sensitive,temperature,suggested,that,existence,oxygen,decreases,exponent,increases,required,activation,energy,critical,slip,decreased,monotonously,following,classic,Hall,Petch,relationship,However,transformation,minimum,then,increased,again,results,are,worth,design,heat,parameters,engineering,applications
AB值:
0.526482
相似文献
Influence of Zr and Mn additions on microstructure and properties of Mg–2.5wt%Cu–Xwt%Zn (X = 2.5, 5 and 6.5) alloys
A.V.Koltygin;V.E.Bazhenov;I.V.Plisetskaya;V.A.Bautin;A.I.Bazlov;N.Y.Tabachkova;O.O.Voropaeva;A.A.Komissarov;V.D.Belov-Foundry Department,National University of Science and Technology(MISiS),Moscow 119049,Russia;Department of Metallurgy Steel,New Production Technologies and Protection of Metals,National University of Science and Technology(MISiS),Moscow119049,Russia;Laboratory of Advanced Green Materials,National University of Science and Technology(MISiS),Moscow 119049,Russia;Department of Materials Science of Semiconductors and Dielectrics,National University of Science and Technology(MISiS),Moscow 119049,Russia;Fianit Laboratory(Laser Materials and Technology Research Center at GPI),Prokhorov General Physics Institute RAS,Moscow 119991,Russia;Laboratory of Hybrid Nanostructured Materials,National University of Science and Technology(MISiS),Moscow 119049,Russia;Laboratory of Medical Bioresorption and Bioresistance,Moscow State University of Medicine and Dentistry,Moscow 127473,Russia
In situ neutron diffraction unravels deformation mechanisms of a strong and ductile FeCrNi medium entropy alloy
L.Tang;F.Q.Jiang;J.S.Wróbel;B.Liu;S.Kabra;R.X.Duan;J.H.Luan;Z.B.Jiao;M.M.Attallah;D.Nguyen-Manh;B.Cai-School of Metallurgy and Materials,University of Birmingham,B15 2TT,United Kingdom;Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;Faculty of Materials Science and Engineering,Warsaw University of Technology,ul.Wo?oska 141,Warsaw 02-507,Poland;State Key Laboratory for Powder Metallurgy,Central South University,Changsha 410083,China;Rutherford Appleton Laboratory,ISIS Facility,Didcot OX11 0QX,United Kingdom;Department of Materials Science and Engineering,City University of Hong Kong,Kowloon,Hong Kong,China;Department of Mechanical Engineering,The Hong Kong Polytechnic University,Hung Hom,Hong Kong,China;CCFE,United Kingdom Atomic Energy Authority,Abingdon,Oxfordshire OX14 3DB,United Kingdom
A superior strength-ductility synergy of Al0.1CrFeCoNi high-entropy alloy with fully recrystallized ultrafine grains and annealing twins
Jiahao Li;Kejie Lu;Xiaojun Zhao;Xinkai Ma;Fuguo Li;Hongbo Pan;Jieming Chen-Key Laboratory of Advanced Technologies of Materials,Ministry of Education,School of Materials Science and Engineering,Southwest Jiaotong University,Chengdu 610031,China;Shenzhen Institute of Southwest Jiaotong University,Shenzhen 518000,China;State Key Laboratory of Solidification Processing,School of Materials Science and Engineering,Northwestern Polytechnical University,Xi'an 710072,China;Anhui Province Key Laboratory of Metallurgical Engineering& Resources Recycling(Anhui University of Technology),243002 Maanshan,China;Luoyang Ship Material Research Institute,Luoyang 471023,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。