Protection Performance of Plasma Sprayed Al2O3-13 wt％TiO2 Coating Sealed with an Organic-inorganic Hybrid Agent
文献摘要：
An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al2O3-13 wt％TiO2 coating, and conventional silicone agent was also used for comparison. Protection performance of the coatings was comprehensively evaluated based on both anti-corrosion and anti-biofouling properties. The results reveal that the sealing treatment is remarkably useful to decrease the porosity of the coating, and the porosity of the coating sealed with the hybrid agent is only 0.035％. Immersion corrosion test and Tafel polarization test reveal that the sealed coating with the hybrid agent exhibits a better corrosion resistance by compared with the coating sealed with silicone agent. The corrosion current density icorr of the hybrid agent sealed coating is only 0.7×10-6 A?cm-2. Moreover, anti-biofouling tests both in the outdoor analogue hydraulic environment and in the natural marine environment prove that the mentioned novel coating presents a better combination of corrosion resistance and anti-biofouling property by compared with the other coatings, and it could be used as a protection of metal components in the marine environment.
文献关键词：
中图分类号：
作者姓名：
ZHANG Kaicheng;ZHOU Zehua;DENG Yong;WANG Guangyu;WANG Zehua;WU Lintao;YANG Guangheng
作者机构：
College of Mechanics and Materials,Hohai University,Nanjing 211100,China;Chengdu Customs Technical Centre,Chengdu 610041,China
文献出处：
引用格式：
[1]ZHANG Kaicheng;ZHOU Zehua;DENG Yong;WANG Guangyu;WANG Zehua;WU Lintao;YANG Guangheng-.Protection Performance of Plasma Sprayed Al2O3-13 wt％TiO2 Coating Sealed with an Organic-inorganic Hybrid Agent)[J].武汉理工大学学报（材料科学版）（英文版）,2022(03):331-335
A类：
Sealed
B类：
Protection,Performance,Plasma,Sprayed,Al2O3,wt,TiO2,Coating,Organic,inorganic,Hybrid,Agent,An,hybrid,sealing,agent,was,fabricated,used,plasma,sprayed,conventional,silicone,also,comparison,performance,coatings,comprehensively,evaluated,both,anti,corrosion,biofouling,properties,results,reveal,that,treatment,remarkably,useful,decrease,porosity,sealed,only,Immersion,Tafel,polarization,exhibits,better,resistance,by,compared,current,density,icorr,Moreover,tests,outdoor,analogue,hydraulic,environment,natural,marine,prove,mentioned,novel,presents,combination,property,other,could,protection,metal,components
AB值：
0.468501
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。