Tribological and Electrochemical Corrosion Properties of CNT-Incorporated Plasma Electrolytic Oxidation(PEO)Coatings on AZ80 Magnesium Alloy
文献摘要：
Plasma electrolytic oxidation(PEO)coatings were carried out in silicate-based electrolyte embedded with various amounts of carbon nanotube(CNT)additives(0,0.5,1,2 and 4 g/L)on AZ80 magnesium alloy substrate.Microstructure,tribological and electrochemical corrosion properties of the coated specimens were investigated.The results demonstrated that the increasing CNT additions into the electrolyte resulted in a gradual increase in the thickness of PEO-coating layer.The CNT addition to the electrolyte by 0.5 g/L resulted in a slight decrease in the roughness of PEO-coating above which it continually increased.Wear resistance of the PEO-coated specimens showed a gradual improvement with increasing CNT-incorporation within the coating.The electrochemical corrosion tests revealed that the best corrosion resistance was found after the CNT addition into the electrolyte by 0.5 g/L due to the better roughness values,more homogenous coating layers and less pore formation.
文献关键词：
中图分类号：
作者姓名：
Rabia Kara;Huseyin Zengin
作者机构：
Department of Metallurgical and Materials Engineering,Karabuk University,78050 Karabuk,Turkey
文献出处：
引用格式：
[1]Rabia Kara;Huseyin Zengin-.Tribological and Electrochemical Corrosion Properties of CNT-Incorporated Plasma Electrolytic Oxidation(PEO)Coatings on AZ80 Magnesium Alloy)[J].金属学报（英文版）,2022(07):1195-1206
A类：
B类：
Tribological,Electrochemical,Corrosion,Properties,CNT,Incorporated,Plasma,Electrolytic,Oxidation,PEO,Coatings,AZ80,Magnesium,Alloy,electrolytic,oxidation,coatings,were,carried,out,silicate,electrolyte,embedded,various,amounts,carbon,nanotube,additives,magnesium,alloy,substrate,Microstructure,tribological,electrochemical,corrosion,properties,coated,specimens,investigated,results,demonstrated,that,increasing,additions,into,resulted,gradual,thickness,by,slight,decrease,roughness,above,which,continually,increased,Wear,resistance,showed,improvement,incorporation,within,tests,revealed,best,was,found,after,due,better,values,more,homogenous,layers,less,pore,formation
AB值：
0.600631
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。