Facile synthesis of Ni-doped SnO2 nanorods and their high gas sensitivity to isopropanol
文献摘要：
In this work,pure SnO2 and Ni-doped SnO2 nanorods were synthesized through a one-step template-free hydrothermal method and then used to detect isopropanol.Sensors fabricated with the Ni-doped SnO2 nanocomposites showed the best gas sensing performance when the Ni doping amount was 1.5 mol.％.The response reached 250 at 225℃,which was approximately 8.3 times higher than that of the pure SnO2 nanorods.The limit of detection for isopropanol was as low as 10 ppb at the optimum working temperature.In addition,it also displayed good selectivity and excellent reproducibility.It is believed that the enhanced isopropanol sensing behavior benefit from the increased oxygen defects and larger specific surface area by Ni doping.
文献关键词：
中图分类号：
作者姓名：
Yanqiu YU;Shantang LIU
作者机构：
Key Laboratory for Green Chemical Process(Ministry of Education),School of Chemistry and Environmental Engineering,Wuhan Institute of Technology,Wuhan 430073,China
文献出处：
引用格式：
[1]Yanqiu YU;Shantang LIU-.Facile synthesis of Ni-doped SnO2 nanorods and their high gas sensitivity to isopropanol)[J].材料学前沿,2022(01):87-97
A类：
B类：
Facile,synthesis,doped,SnO2,nanorods,their,gas,sensitivity,isopropanol,In,this,pure,were,synthesized,through,one,step,template,free,hydrothermal,method,then,used,Sensors,fabricated,nanocomposites,showed,best,sensing,performance,when,doping,amount,was,response,reached,which,approximately,times,higher,than,that,limit,detection,low,ppb,optimum,working,temperature,addition,also,displayed,good,selectivity,excellent,reproducibility,It,believed,enhanced,behavior,benefit,from,increased,oxygen,defects,larger,specific,surface,area,by
AB值：
0.616529
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。