Effect of Heat Treatment on the Microstructure,Mechanical Properties and Corrosion Resistance of Selective Laser Melted 304L Stainless Steel
文献摘要:
The influence of heat treatment holding temperatures from 600 to 1300℃on the microstructure,mechanical properties and corrosion resistance in selective laser melted(SLMed)304L stainless steel is investigated in this work.The results reveal that there is no remarkable microstructure change after holding at 600℃for 2 h,while recrystallization leads to a slight decrease in grain size in the temperature range of 700-900℃.The heat treatment at temperatures from 1000 to 1300℃for 2 h obviously affects the morphology of grains in SLMed 304L stainless steel.Combining effects of grain coarsening,delta-ferrite(8)phases reduction and residual stress release during heat treatment lead to the reduction of yield strength and an increasing elongation.The elongation of the samples heat treated at 800℃for 2 h is,however,significantly decreased due to the increase in the amount of sigma(σ)phase.A remarkable increase in the amount of δ ferrite results in an increase in yield strength but a decrease in ductility after heat treatment at 1300℃for 2 h.The corrosion resistance of the samples heat treated at 1300℃is significantly improved due to the substantial reduction of brittle phase(σ).There is no obvious effect of the presence of 8 ferrite on corrosion behavior.
文献关键词:
作者姓名:
Fan Yang;Daigen Zhu;Menglei Jiang;Hui Liu;Shiri Guo;Qingyan Wang;Hui Wang;Kai Zhang;Aijun Huang;Juan Hou
作者机构:
School of Materials and Chemistry,University of Shanghai for Science and Technology,Shanghai 200093,China;Institute for Advanced Study,Chengdu University,Chengdu 610106,China;Monash Centre for Additive Manufacturing(MCAM),Monash University,Notting Hill,VIC 3168,Australia;State Key Laboratory of Nuclear Power Safety Monitoring Technology and Equipment,Shenzhen 518172,China
引用格式:
[1]Fan Yang;Daigen Zhu;Menglei Jiang;Hui Liu;Shiri Guo;Qingyan Wang;Hui Wang;Kai Zhang;Aijun Huang;Juan Hou-.Effect of Heat Treatment on the Microstructure,Mechanical Properties and Corrosion Resistance of Selective Laser Melted 304L Stainless Steel)[J].金属学报(英文版),2022(10):1688-1702
A类:
Melted,SLMed
B类:
Effect,Heat,Treatment,Microstructure,Mechanical,Properties,Corrosion,Resistance,Selective,Laser,304L,Stainless,Steel,influence,heat,treatment,holding,temperatures,from,microstructure,mechanical,properties,corrosion,resistance,selective,laser,melted,stainless,steel,investigated,this,work,results,reveal,that,there,no,remarkable,change,after,while,recrystallization,leads,slight,size,range,obviously,affects,morphology,grains,Combining,effects,coarsening,delta,ferrite,phases,reduction,residual,stress,release,during,yield,strength,increasing,elongation,samples,treated,however,significantly,decreased,due,increase,amount,sigma,but,ductility,improved,substantial,brittle,There,presence,behavior
AB值:
0.494301
相似文献
Influence of Zr and Mn additions on microstructure and properties of Mg–2.5wt%Cu–Xwt%Zn (X = 2.5, 5 and 6.5) alloys
A.V.Koltygin;V.E.Bazhenov;I.V.Plisetskaya;V.A.Bautin;A.I.Bazlov;N.Y.Tabachkova;O.O.Voropaeva;A.A.Komissarov;V.D.Belov-Foundry Department,National University of Science and Technology(MISiS),Moscow 119049,Russia;Department of Metallurgy Steel,New Production Technologies and Protection of Metals,National University of Science and Technology(MISiS),Moscow119049,Russia;Laboratory of Advanced Green Materials,National University of Science and Technology(MISiS),Moscow 119049,Russia;Department of Materials Science of Semiconductors and Dielectrics,National University of Science and Technology(MISiS),Moscow 119049,Russia;Fianit Laboratory(Laser Materials and Technology Research Center at GPI),Prokhorov General Physics Institute RAS,Moscow 119991,Russia;Laboratory of Hybrid Nanostructured Materials,National University of Science and Technology(MISiS),Moscow 119049,Russia;Laboratory of Medical Bioresorption and Bioresistance,Moscow State University of Medicine and Dentistry,Moscow 127473,Russia
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。