High Temperature Plastic Deformation Behavior and Brittle Mechanism of S450EW Steel
文献摘要：
High-temperature tensile tests were conducted for high corrosion resistant weathering steel S450EW. The morphologies of fracture microstructures, dislocations and precipitates were investigated by field emission scanning electron microscopy and transmission electron microscopy. The high-temperature plastic deformation behavior and brittle mechanism of S450EW steel were also studied. The experimental results show that the ductility troughs appear at 700-850℃ and 650-900℃ when the strain rates are 3×10-3 and 1.5×10-2 s-1, respectively. With the increase of strain rates, the ductility trough moves to the lower temperature side. The hot ductility is best when the cooling rate is 5 ℃/s before deformation at 750 ℃ and the area reduction rate reaches 60.56％. Fine second phase particles and inclusions precipitated before and during deformation provide effective core positions for microcracks or microvoids formation during deformation process. It is also easy to cause stress concentration which results in microcracks or microvoids between grains during deformation and ultimately causes damage along the grain boundaries. The precipitated particles inhibit austenite dynamic recrystallization and therefore enhance intergranular fracture along austenite grain boundaries. The deformation induced proeutectoid ferrite films distribute along the austenite grain boundaries hinder the dynamic recrystallization. The deformation concentrated on network ferrite films produces damage of grain boundaries.
文献关键词：
中图分类号：
作者姓名：
CHEN Jiping;HU Xuewen;QIAN Jianqing
作者机构：
School of Metallurgical Engineering,Anhui University of Technology,Maanshan 243032,China;Technology Center of Masteel,Maan-shan 243000,China
文献出处：
引用格式：
[1]CHEN Jiping;HU Xuewen;QIAN Jianqing-.High Temperature Plastic Deformation Behavior and Brittle Mechanism of S450EW Steel)[J].武汉理工大学学报（材料科学版）（英文版）,2022(04):722-729
A类：
Brittle,S450EW,troughs,proeutectoid
B类：
High,Temperature,Plastic,Deformation,Behavior,Mechanism,Steel,temperature,tensile,tests,were,conducted,high,corrosion,resistant,weathering,steel,morphologies,fracture,microstructures,dislocations,precipitates,investigated,by,field,emission,scanning,electron,microscopy,transmission,plastic,deformation,behavior,brittle,mechanism,also,studied,experimental,results,show,that,ductility,appear,when,strain,rates,respectively,With,increase,moves,lower,side,hot,best,cooling,before,area,reduction,reaches,Fine,second,phase,particles,inclusions,precipitated,during,provide,effective,core,positions,microcracks,microvoids,process,It,easy,stress,concentration,which,between,grains,ultimately,causes,damage,along,boundaries,inhibit,austenite,dynamic,recrystallization,therefore,enhance,intergranular,induced,ferrite,films,distribute,hinder,concentrated,network,produces
AB值：
0.534413
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。