Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment
文献摘要：
For additive manufactured aluminum alloys,the inferior mechanical properties along the building direc-tion have been a serious weakness.In this study,an optimized heat treatment was developed as a simple and effective solution.The effects of direct aging on microstructure and mechanical properties along the building direction of AISi10Mg samples produced via selective laser melting(SLM)were investigated.The results showed that,compared with the conventional heat treatment at elevated temperatures,direct aging at temperatures of 130-190℃could retain the fine grain microstructure of SLM samples and pro-mote further precipitation of Si phase,however,the growth of pores occurred during direct aging.With increasing aging temperature,while finer cell structures were obtained,more and larger pores were de-veloped,resulting in decreased density of the samples.Two types of pore formation mechanisms were identified.Considering the balance between the refinement of cell structure and the growth of pores,aging at 130℃was determined as the optimized heat treatment for SLM AISi10Mg samples.The tensile strength along the building direction of the 130℃aged sample was increased from 403 MPa to 451 MPa,with relatively high elongation of 6.5％.
文献关键词：
中图分类号：
作者姓名：
H.Zhang;Y.Wang;J.J.Wang;D.R.Ni;D.Wang;B.L.Xiao;Z.Y.Ma
作者机构：
Shi-changxu Innovation Center for Advanced Materials,Institute of Metal Research,Chinese Academy of Sciences,72 Wenhua Road,Shenyang 110016,China;College of Materials Science and Engineering,Shenyang Aerospace University,37 Daoyi South Avenue,Shenyang 110136,China
文献出处：
引用格式：
[1]H.Zhang;Y.Wang;J.J.Wang;D.R.Ni;D.Wang;B.L.Xiao;Z.Y.Ma-.Achieving superior mechanical properties of selective laser melted AlSi10Mg via direct aging treatment)[J].材料科学技术（英文版）,2022(13):226-235
A类：
B类：
Achieving,superior,mechanical,properties,selective,laser,melted,AlSi10Mg,via,aging,treatment,For,additive,manufactured,aluminum,alloys,inferior,along,building,have,been,serious,weakness,In,this,study,optimized,heat,was,developed,simple,effective,solution,effects,microstructure,direction,AISi10Mg,samples,produced,melting,SLM,were,investigated,results,showed,that,compared,conventional,elevated,temperatures,could,retain,grain,mote,further,precipitation,phase,however,growth,pores,occurred,during,With,increasing,while,finer,cell,structures,obtained,more,larger,resulting,decreased,density,Two,types,formation,mechanisms,identified,Considering,balance,between,refinement,determined,tensile,strength,aged,increased,from,relatively,high,elongation
AB值：
0.546173
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。