Effect of Nanoscale Cu-Riched Clusters on Strength and Impact Toughness in a Tempered Cu-Bearing HSLA Steel
文献摘要：
The effect of Cu-riched clusters on strength and impact toughness in a tempered Cu-bearing high-strength low-alloy(HSLA)steel is investigated.With increasing the tempering temperature,it is found that the yield strength increases firstly,achiev-ing the maximum value(～1053 MPa)at the tempering temperature of 450℃,and then decreases significantly with the rise of tempering temperature.The tempering temperature-dependent yield strength is closely related to the precipitation of Cu-riched clusters.When tempering at 450℃,the peak strength will be reached as the nanoscale Cu-riched clusters with small size and high number density will cause a strong precipitation strengthening(～492 MPa)due to the dislocation shearing mechanism.However,the Cu-riched clusters will coarsen with further increasing tempering temperature,resulting in obvious decrement of yield strength owing to the dislocation bypassing mechanism.Compared with the yield strength,the variation in impact energy displays an inverse tendency and the impact energy is only 7 J for the sample tempered at 450℃.The fracture mode can be well explained by the competition between the cleavage fracture strength(σF)and"yield strength"(σY).Although transgranular cleavage fracture can be found in samples tempered at 450 and 550℃,the crack propagation along the lath boundaries is prevented in the sample tempered at 550℃.The reason is that the number density of Cu-riched clusters at lath boundaries decreases and the segregation of Mo element at the lath boundaries is induced,which will increase the bonding energy.
文献关键词：
中图分类号：
作者姓名：
Yubin Du;Xiaofeng Hu;Yuanyuan Song;Yangpeng Zhang;Lijian Rong
作者机构：
CAS Key Laboratory of Nuclear Materials and Safety Assessment,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;School of Materials Science and Engineering,University of Science and Technology of China,Shenyang 110016,China
文献出处：
引用格式：
[1]Yubin Du;Xiaofeng Hu;Yuanyuan Song;Yangpeng Zhang;Lijian Rong-.Effect of Nanoscale Cu-Riched Clusters on Strength and Impact Toughness in a Tempered Cu-Bearing HSLA Steel)[J].金属学报（英文版）,2022(04):537-550
A类：
Riched,Tempered
B类：
Effect,Nanoscale,Clusters,Strength,Impact,Toughness,Bearing,HSLA,Steel,effect,riched,clusters,impact,toughness,tempered,bearing,high,low,alloy,steel,investigated,With,increasing,tempering,temperature,found,that,yield,increases,firstly,achiev,maximum,value,decreases,significantly,rise,dependent,closely,related,precipitation,When,peak,will,reached,nanoscale,small,size,number,density,cause,strong,strengthening,due,dislocation,shearing,mechanism,However,coarsen,further,resulting,obvious,decrement,owing,bypassing,Compared,variation,energy,displays,inverse,tendency,only,fracture,mode,well,explained,competition,between,cleavage,Although,transgranular,samples,crack,propagation,along,lath,boundaries,prevented,reason,segregation,Mo,element,induced,which,bonding
AB值：
0.44694
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。