Tribological performance and scuffing behaviors of several automobile piston rings mating with chrome-plated cylinder liner
文献摘要：
The friction and wear properties,as well as the scuffing resistance,of different piston-ring coatings mating with a chrome-plated cylinder liner were investigated.Interrupted wear tests under the lubricant starvation condition were conducted to examine the wear behavior of Cr-diamond coating(GDC)and diamond-like coating(DLC).The results indicated that the DLC coating had outstanding tribological properties(small coefficient of friction and wear loss)at 150℃,while the GDC coating exhibited better performance at an elevated temperature(240℃).The DLC coating had a better scuffing resistance;no material adhesion occurred for 70 min under the unlubricated condition.The interrupted wear behaviors revealed that the scuffing process of the GDC coating involved the consumption of lubricant oil with relatively stable wear,a reduction in the friction force,and the occurrence of scuffing,in sequence.In contrast,although the friction force also increased after a short period of weak friction,no scuffing was observed.This is attributed to the formation of a mixed oxide and graphitic C tribolayer.
文献关键词：
中图分类号：
作者姓名：
Zeyu MA;Ruoxuan HUANG;Xiaoshuai YUAN;Yan SHEN;Jiujun XU
作者机构：
Department of Materials Science and Engineering,Dalian Maritime University,Dalian 116026,China;China North Engine Research Institute(Tianjin),Tianjin 300400,China;Marine Engineering College,Dalian Maritime University,Dalian 116026,China;Key Lab of Ship-Machinery Maintenance&Manufacture,Dalian Maritime University,Dalian 116026,China
文献出处：
引用格式：
[1]Zeyu MA;Ruoxuan HUANG;Xiaoshuai YUAN;Yan SHEN;Jiujun XU-.Tribological performance and scuffing behaviors of several automobile piston rings mating with chrome-plated cylinder liner)[J].摩擦（英文）,2022(08):1245-1257
A类：
scuffing,unlubricated,tribolayer
B类：
Tribological,performance,behaviors,several,automobile,piston,rings,mating,chrome,plated,cylinder,liner,friction,wear,properties,well,resistance,different,coatings,were,investigated,Interrupted,tests,under,lubricant,starvation,condition,conducted,examine,diamond,GDC,like,DLC,results,indicated,that,had,outstanding,tribological,small,coefficient,loss,while,exhibited,better,elevated,temperature,no,material,adhesion,occurred,interrupted,revealed,process,involved,consumption,oil,relatively,stable,reduction,force,occurrence,sequence,contrast,although,also,increased,after,short,period,weak,was,observed,This,attributed,formation,mixed,oxide,graphitic
AB值：
0.484641
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。