Tribological performance of hydrogenated diamond-like carbon coating deposited on superelastic 60NiTi alloy for aviation self-lubricating spherical plain bearings
文献摘要：
It is imperative to develop a novel matching of metallic substrate and self-lubricating coating for aircraft spherical plain bearing in a wide range of service conditions.As a new type of superelastic material,60NiTi alloy meets the performance requirements of aerospace bearing materials,but exhibits poor tribological performance,especially under the conditions of dry sliding friction.A Hydrogenated Diamond-Like Carbon(H-DLC)coating was deposited on the 60NiTi alloy to improve its tribological performance.The microstructure and mechanical behavior of the 60NiTi alloy and its H-DLC coating were explored.Results show that improvement of friction and wear performance of the H-DLC coating deposited on the 60NiTi substrate is mainly achieved by graphitization at the friction interface and the transfer film produced on the counterpart ball.The increased friction load leads to intensification of graphitization at the friction interface and for-mation of continuous and compact transfer film on the surface of the counterpart ball.
文献关键词：
中图分类号：
作者姓名：
Yefei ZHOU;Zhihao CHEN;Zhonghui HU;Lei LI;Qingxiang YANG;Xiaolei XING
作者机构：
College of Mechanical Engineering,Yanshan University,Qinhuangdao 066004,China;State Key Laboratory of Metastable Materials Science&Technology,Yanshan University,Qinhuangdao 066004,China;Aviation Key Laboratory of Science and Technology on Generic Technology of Self-Lubricating Spherical Plain Bearing,Yanshan University,Qinhuangdao 066004,China;AVIC the First Aircraft Institute,Xi'an 710089,China;Northwest Institute for Nonferrous Metal Research,Xi'an 710016,China
文献出处：
引用格式：
[1]Yefei ZHOU;Zhihao CHEN;Zhonghui HU;Lei LI;Qingxiang YANG;Xiaolei XING-.Tribological performance of hydrogenated diamond-like carbon coating deposited on superelastic 60NiTi alloy for aviation self-lubricating spherical plain bearings)[J].中国航空学报（英文版）,2022(12):309-320
A类：
B类：
Tribological,performance,hydrogenated,diamond,like,carbon,coating,deposited,superelastic,60NiTi,alloy,aviation,self,lubricating,spherical,plain,bearings,It,is,imperative,develop,novel,matching,metallic,substrate,aircraft,wide,range,service,conditions,new,type,meets,requirements,aerospace,materials,but,exhibits,poor,tribological,especially,under,dry,sliding,friction,Hydrogenated,Diamond,Like,Carbon,DLC,was,microstructure,mechanical,behavior,were,explored,Results,show,that,improvement,wear,mainly,achieved,by,graphitization,interface,transfer,film,produced,counterpart,ball,increased,load,leads,intensification,mation,continuous,compact,surface
AB值：
0.537945
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。