Relationship between crystallographic structure of complex inclusions MgAl2O4/Ti2O3/MnS and improved toughness of heat-affected zone in shipbuilding steel
文献摘要：
In accordance with the minimum degree of disregistry mechanism in oxide metallurgy,the intragranular acicular ferrite(IAF)generated by microalloying elements in austenite was studied.Herein,the effect of Mg treatment on the microstructure and toughness of the heat-affected zone(HAZ)in shipbuilding steel was investigated.Mg treatment produced inclusions that influenced the formation of acicular ferrite in the microstructure.This refined the HAZ microstructure and improved its toughness.Electron backscatter diffraction was used to determine the oxides of titanium and the MgO·Al2O3 or MgAl2O4 complex inclusions that induced the formation of IAF.MnS precipitated on MgAl2O4 on a specific habit plane and in a specific direction.MnS had a specific orientation relationship with MgAl2O4,i.e.,{100}MgAl2O4//{100}MnS The 35-mm-thick plate obtained in the industrial test after welding at a welding heat input of 120 kJ/cm had an average impact absorbed energy of 282.7 J at-40℃and 2 mm from the weld joint in the HAZ.The two-dimensional disregistry index between inclusions can be used as the basis for controlling their distribution and adsorption force.Microalloy addition in the order of Al-Mg-Ti is key to obtaining abundant dispersion and fine nucleation in austenite.
文献关键词：
中图分类号：
作者姓名：
Yan Wang;Li-guang Zhu;Jin-xia Huo;Qing-jun Zhang;Yao-guang Wu;Wei Chen;Shuo-ming Wang
作者机构：
College of Metallurgy and Energy,North China University of Science and Technology,Tangshan 063210,Hebei,China;College of Materials Science and Engineering,Hebei University of Science and Technology,Shijiazhuang 050018,Hebei,China;China Analysis and Testing Center,North China University of Science and Technology,Tangshan 063210,Hebei,China;MCC Capital Engineering&Research Incorporation Limited,Metallurgical Engineering Consulting and Design Division,Beijing 100176,China
文献出处：
引用格式：
[1]Yan Wang;Li-guang Zhu;Jin-xia Huo;Qing-jun Zhang;Yao-guang Wu;Wei Chen;Shuo-ming Wang-.Relationship between crystallographic structure of complex inclusions MgAl2O4/Ti2O3/MnS and improved toughness of heat-affected zone in shipbuilding steel)[J].钢铁研究学报（英文版）,2022(08):1277-1290
A类：
disregistry,Microalloy
B类：
Relationship,between,crystallographic,complex,inclusions,MgAl2O4,Ti2O3,MnS,improved,toughness,heat,affected,zone,shipbuilding,steel,In,accordance,minimum,degree,mechanism,metallurgy,intragranular,acicular,ferrite,IAF,generated,by,microalloying,elements,austenite,was,studied,Herein,effect,treatment,microstructure,HAZ,investigated,produced,that,influenced,formation,This,refined,its,Electron,backscatter,diffraction,used,determine,oxides,titanium,MgO,Al2O3,induced,precipitated,specific,habit,plane,direction,had,orientation,relationship,thick,plate,obtained,industrial,test,after,welding,input,kJ,average,impact,absorbed,energy,from,joint,two,dimensional,can,basis,controlling,their,distribution,adsorption,force,addition,order,key,obtaining,abundant,dispersion,nucleation
AB值：
0.521438
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。