Microstructure evolution and acicular ferrite nucleation in inclusion-engineered steel with modified MgO@C nanoparticle addition
文献摘要：
To investigate the effect of surface-modified nanoparticles(NPs)on the inclusion refinement and mi-crostructure evolution,deoxidized experiment ingots with different amounts of modified NPs were man-ufactured under different cooling conditions.Laser scanning confocal microscope(LSCM)was hereby used for in-situ observation of the phase transition and microstructural evolution during heat cycle process.The results revealed that the inclusion size was always smaller under water quenching than under air cooling,and the number of inclusions was greater under water quenching.After NP addition,the nucle-ant inclusions were identified as MgAl2O4 spinel and irregular TiN inclusion from SEM-EDS measurement and equilibrium calculations using Factsage thermodynamic software.The higher cooling rate under water quenching resulted in less polygonal ferrite decrease and the formation of bainite in the steel.The LSCM experiments showed that ferrite side plates(FSP)always formed on the boundary prior to the formation of acicular ferrite(AF)on the intragranular inclusions,and the start transformation temperatures of FSP and AF phases both lowered after NP addition.The higher cooling rate and NP addition contributed to AF formation and increased the degree of interlocking of the AF phase.Finally,the relationship between the characteristics of inclusions and the kinetics of AF was investigated.
文献关键词：
中图分类号：
作者姓名：
Hao Guo;Shufeng Yang;Tiantian Wang;Hang Yuan;Yanling Zhang;Jingshe Li
作者机构：
State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing,Beijing 100083,China;Beijing Key Laboratory of Special Melting and Preparation of High-end Metals,University of Science and Technology Beijing,Beijing 100083,China;Department of Materials Engineering,KU Leuven,Kasteelpark Arenberg 44,3001 Leuven,Belgium;School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China
文献出处：
引用格式：
[1]Hao Guo;Shufeng Yang;Tiantian Wang;Hang Yuan;Yanling Zhang;Jingshe Li-.Microstructure evolution and acicular ferrite nucleation in inclusion-engineered steel with modified MgO@C nanoparticle addition)[J].材料科学技术（英文版）,2022(04):277-287
A类：
crostructure,deoxidized
B类：
Microstructure,evolution,acicular,ferrite,nucleation,engineered,steel,modified,MgO,addition,To,effect,surface,nanoparticles,NPs,refinement,ingots,different,amounts,man,ufactured,under,cooling,conditions,Laser,scanning,confocal,microscope,LSCM,was,hereby,used,situ,observation,transition,microstructural,during,heat,cycle,process,results,revealed,that,size,always,smaller,water,quenching,than,air,number,inclusions,greater,After,ant,identified,MgAl2O4,spinel,irregular,TiN,from,EDS,measurement,equilibrium,calculations,using,Factsage,thermodynamic,software,higher,rate,resulted,less,polygonal,decrease,bainite,experiments,showed,side,plates,FSP,formed,boundary,prior,AF,intragranular,start,transformation,temperatures,phases,both,lowered,after,contributed,increased,degree,interlocking,Finally,relationship,between,characteristics,kinetics,investigated
AB值：
0.547208
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。