Corrosion resistance of BN-ZrO2 ceramics with different additives by molten steel
文献摘要:
BN-ZrO2 ceramics with different additives such as SiC,Al2O3 and MgAl2O4 were fabricated by hot pressing sintering process to study sintering properties and corrosion resistance by the rotary immersion molten steel test.The results showed that SiC,Al2O3 and MgAl2O4 can improve the sintering properties of BN-ZrO2 ceramics;especially,the introduction of SiC can significantly improve the hardness of the material;thus,the above compounds will help to improve the wear resistance of BN-ZrO2 ceramics.The exposed oxide layer is in contact with molten steel and forms liquid phase after BN oxidation and B2O3 volatilization,additives can significantly affect the properties of liquid phase,and m-ZrO2 grains are sintered and grown by dissolution-precipitation mechanism by liquid phase.Consequently,Al2O3 and MgAl2O4 are more conducive to the formation of working layer with solid skeleton,which determines the corrosion resistance of BN-ZrO2 ceramics.
文献关键词:
作者姓名:
Fan Qian;Hua-long Li;Wen-gang Yang;Hai-rong Guo;Guo-qi Liu;Hong-xia Li;Bei-yue Ma
作者机构:
State Key Laboratory of Advanced Refractories,Sinosteel Luoyang Institute of Refractories Research Co.,Ltd.,Luoyang 471039,Henan,China;Institute of Research of Iron and Steel,Shasteel,Zhangjiagang 215625,Jiangsu,China;School of Metallurgy,Northeastern University,Shenyang 110819,Liaoning,China
引用格式:
[1]Fan Qian;Hua-long Li;Wen-gang Yang;Hai-rong Guo;Guo-qi Liu;Hong-xia Li;Bei-yue Ma-.Corrosion resistance of BN-ZrO2 ceramics with different additives by molten steel)[J].钢铁研究学报(英文版),2022(07):1101-1109
A类:
B类:
Corrosion,resistance,BN,ZrO2,ceramics,different,additives,by,molten,steel,such,SiC,Al2O3,MgAl2O4,were,fabricated,hot,pressing,sintering,process,study,properties,corrosion,rotary,immersion,test,results,showed,that,improve,especially,introduction,significantly,hardness,material,thus,above,compounds,will,help,wear,exposed,oxide,layer,contact,forms,liquid,phase,after,oxidation,B2O3,volatilization,affect,grains,are,sintered,grown,dissolution,precipitation,mechanism,Consequently,more,conducive,formation,working,solid,skeleton,which,determines
AB值:
0.51098
相似文献
Medium-entropy(Me,Ti)0.1(Zr,Hf,Ce)0.9O2(Me=Y and Ta):Promising thermal barrier materials for high-temperature thermal radiation shielding and CMAS blocking
Shuaihang Qiu;Huimin Xiang;Fu-Zhi Dai;Hailong Wang;Muzhang Huang;Chunlei Wan;Qing Meng;Jiangtao Li;Xiaohui Wang;Yanchun Zhou-Science and Technology on Advanced Functional Composite Laboratory,Aerospace Research Institute of Materials and Processing Technology,Beijing 100076,China;State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology,Wuhan 430070,China;School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450001,China;State Key Lab of New Ceramics and Fine Processing,School of Materials Science and Engineering,Tsinghua University,Beijing 100084,China;Technical Institute of Physics and Chemistry,Chinese Academy of Sciences,Beijing 100190,China;Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。