Microstructure and properties of TiB2-Ni coatings with different binder phase contents deposited by HVOF spray process
文献摘要：
TiB2-Ni coatings with different binder phase contents were sprayed on Q235 substrate by a high-velocity oxygen-fuel(HVOF)method using ball-milled powders.The microstructure,phase compositions,as well as thermal shock behavior,abrasive wear,and corrosion resistance to molten Al-12.07 wt％Si alloy performances of as-sprayed coatings were investigated.The results show that the three TiB2-Ni coatings structure is dense with low porosity,and the main phase compositions of the coatings are TiB2 and Ni similar to those of original powder.The coatings that have superior performance of thermal shock resistance have good bond to the substrate with no change in thick-ness and microstructure of coatings.Meanwhile,the coat-ings also have good durability in the molten Al-12.07 wt％Si after 60-h immersion test.And the mass loss of Q235 steel is five times as much as that of TiB2-50Ni coatings after abrasive wear test.
文献关键词：
中图分类号：
作者姓名：
Xiao Chen;Hong-Tao Wang;Gang-Chang Ji;Xiao-Bo Bai;Wei Fu
作者机构：
School of Mechanical and Materials Engineering,Jiujiang University,Jiujiang 332005,China
文献出处：
引用格式：
[1]Xiao Chen;Hong-Tao Wang;Gang-Chang Ji;Xiao-Bo Bai;Wei Fu-.Microstructure and properties of TiB2-Ni coatings with different binder phase contents deposited by HVOF spray process)[J].稀有金属（英文版）,2022(04):1385-1393
A类：
50Ni
B类：
Microstructure,properties,TiB2,coatings,different,binder,phase,contents,deposited,by,HVOF,process,were,sprayed,Q235,substrate,high,velocity,oxygen,fuel,method,using,ball,milled,powders,microstructure,compositions,well,thermal,shock,behavior,abrasive,wear,corrosion,resistance,molten,wt,Si,alloy,performances,investigated,results,show,that,three,dense,low,porosity,main,are,similar,those,original,have,superior,good,bond,no,change,thick,ness,Meanwhile,also,durability,after,immersion,test,And,mass,loss,steel,five,times,much
AB值：
0.497433
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。