Leaching process of phosphorus and iron from steelmaking slag into malic acid solution
文献摘要：
In order to remove phosphorus element from steelmaking slag and decrease iron loss,malic acid was selected as the leaching agent to dissolve steelmaking slag.Firstly,the influences of different factors,such as malic acid concentration,slag particle size,temperature,liquid/solid ratio and stirring speed,on the leaching ratios of phosphorus and iron were studied.Then,the kinetics for the leaching process of phosphorus was analyzed.The results showed that the leaching ratios of phosphorus and iron increase significantly with increasing the malic acid solution concentration and liquid/solid ratio.When the concentration of malic acid solution increases up to 0.01492 mol/L,about 80％phosphorus can be dissolved,and iron leaching ratio is less than 17％.In addition,decreasing slag particle size can obviously increase the leaching ratio of phosphorus.However,temperature and stirring speed have no significant effect on the dissolution of phosphorus and iron.The leaching kinetics of phosphorus follows the unreacted shrinking core model.Diffusion through product layer is the rate-limiting step of the leaching process,and the corresponding apparent activation energy is determined to be 3.32 kJ/mol.Finally,a semi-empirical kinetic equation was established.
文献关键词：
中图分类号：
作者姓名：
Ning-ning Lv;Chang Su;Hui Kong;Hai-chuan Wang;Yuan-chi Dong
作者机构：
Key Laboratory of Metallurgical Emission Reduction and Resources Recycling,Ministry of Education,Anhui University of Technology,Ma'anshan 243002,Anhui,China;School of Metallurgical Engineering,Anhui University of Technology,Ma'anshan 243002,Anhui,China
文献出处：
引用格式：
[1]Ning-ning Lv;Chang Su;Hui Kong;Hai-chuan Wang;Yuan-chi Dong-.Leaching process of phosphorus and iron from steelmaking slag into malic acid solution)[J].钢铁研究学报（英文版）,2022(06):951-960
A类：
B类：
Leaching,process,phosphorus,iron,from,steelmaking,slag,into,malic,acid,In,order,remove,element,decrease,loss,was,selected,leaching,agent,Firstly,influences,different,factors,such,concentration,particle,size,temperature,liquid,solid,stirring,speed,ratios,were,studied,Then,kinetics,analyzed,results,showed,that,significantly,increasing,When,increases,up,about,be,dissolved,less,than,addition,decreasing,obviously,However,have,no,effect,dissolution,follows,unreacted,shrinking,core,model,Diffusion,through,product,layer,rate,limiting,step,corresponding,apparent,activation,energy,determined,kJ,Finally,semi,empirical,equation,established
AB值：
0.459397
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。