Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags
文献摘要：
The rheological behavior of Cr2O3-containing slags was investigated using a rotating cylinder viscometer and the solid fraction and phases of Cr2O3 in molten slags were also calculated and observed at different temperatures.Furthermore,the viscosities of CaO-SiO2-Cr2O3(-10％A12O3)slags were measured from 1703 to 1953 K and the influence of Cr2O3 content on the viscosity and rheological behavior of molten slags was investigated.The calculation revealed that the solid fraction of the molten slags varied with the Cr2O3 content and maximum temperature,and the fluid properties transitioned from Newtonian to non-Newtonian behavior when the solid fraction reached 5％.Moreover,the increase in Cr2O3 content led to an increase in the viscosity as the slags displayed Newtonian flow characteristics and a decrease in the viscosity when slags exhibited non-Newtonian flow characteristics.The viscosity results of Cr2O3-containing slag from 1703 to 1953 K and from 1703 to 1813 K were also discussed with the morphologies.
文献关键词：
中图分类号：
作者姓名：
Fang Yuan;Zheng Zhao;Yan-ling Zhang;Tuo Wu
作者机构：
State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing,Beijing 100083,China
文献出处：
引用格式：
[1]Fang Yuan;Zheng Zhao;Yan-ling Zhang;Tuo Wu-.Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags)[J].钢铁研究学报（英文版）,2022(04):601-611
A类：
B类：
Influence,Cr2O3,content,viscosity,rheological,behavior,containing,slags,was,investigated,using,rotating,cylinder,viscometer,solid,fraction,phases,molten,were,also,calculated,observed,different,temperatures,Furthermore,viscosities,CaO,SiO2,A12O3,measured,from,influence,calculation,revealed,that,varied,maximum,fluid,properties,transitioned,Newtonian,when,reached,Moreover,increase,displayed,flow,characteristics,decrease,exhibited,results,discussed,morphologies
AB值：
0.387778
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。