Rheological model of semisolid Mg2Si/AM60 composites prepared by ultrasonic vibration treatment
文献摘要：
The rheological behavior of semisolid Mg2Si/AM60 composites prepared by ultrasonic vibration treat-ment was investigated.The effects of primary α-Mg solid content,the ultrasonic power and the content of rein-forcement phase Mg2Si on the apparent viscosity of semisolid composites were discussed.The results show that the apparent viscosity of the semisolid composites increa-ses with the increase in α-Mg solid content.Meanwhile,the apparent viscosity decreases with the increase in ultrasonic power,and the reduction amplitude is higher when the solid content is higher.In addition,the apparent viscosity increases with the increase in Mg2Si content.Based on experimental data fitting,the rheological model of semi-solid Mg2Si/AM60 composites prepared by ultrasonic vibration was established.
文献关键词：
中图分类号：
作者姓名：
Yuan-Sheng Rao;Hong Yan;Jun Wan
作者机构：
Department of Materials Processing Engineering,School of Mechanical and Electrical Engineering,Nanchang University,Nanchang 330031,China;Key Laboratory of Light Alloy Preparation and Processing in Nanchang City,Nanchang 330031,China
文献出处：
引用格式：
[1]Yuan-Sheng Rao;Hong Yan;Jun Wan-.Rheological model of semisolid Mg2Si/AM60 composites prepared by ultrasonic vibration treatment)[J].稀有金属（英文版）,2022(08):2783-2788
A类：
B类：
Rheological,model,semisolid,Mg2Si,AM60,composites,prepared,by,ultrasonic,vibration,treatment,rheological,behavior,was,investigated,effects,primary,content,power,rein,forcement,phase,apparent,viscosity,were,discussed,results,show,that,Meanwhile,decreases,reduction,amplitude,higher,when,In,addition,increases,Based,experimental,data,fitting,established
AB值：
0.367556
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。