Evolution of inclusions in a pipeline steel during continuous casting and hot rolling process
文献摘要：
Industrial trials were performed to study the evolution of inclusions in a pipeline steel during the continuous casting and hot rolling process.The main composition of inclusions changed from Al2O3-CaO in the liquid steel to Al2O3-CaO-CaS in the slab,and then to Al2O3-CaS in the rolled plate.Corresponding area fractions of inclusions increased from 47.0×10-6 to 76.7×10-6,and to 144.3×10-6.It was explained by thermodynamic calculations that the thermodynamic equilibrium between inclusions and the steel varied with the temperature.Element contents of Al,Ca,Mg,S,and O in the steel decreased during the solidification and cooling process.Due to the difference in the cooling rate,the transformation ratio of CaS increased from 61％at the slab surface to 95％in the slab center.It was also affected by the size of inclusions as smaller inclusions provided better kinetic conditions.Critical diameters of inclusions for the composition transformation were calculated.For the hot rolling process,the average aspect ratio of inclusions increased from 1.4 in the slab to 2.8 in the rolled plate.During the hot rolling process,a part of inclusions was crushed into small particles of CaS phase and Al2O3-CaO-MgO cores,leading to a decrease in CaS content of inclusions.
文献关键词：
中图分类号：
作者姓名：
Yi Wang;Wei-fu Li;Wen Yang
作者机构：
School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China
文献出处：
引用格式：
[1]Yi Wang;Wei-fu Li;Wen Yang-.Evolution of inclusions in a pipeline steel during continuous casting and hot rolling process)[J].钢铁研究学报（英文版）,2022(01):175-185
A类：
B类：
Evolution,inclusions,pipeline,steel,during,continuous,casting,hot,rolling,process,Industrial,trials,were,performed,study,evolution,main,composition,changed,from,Al2O3,CaO,liquid,CaS,slab,then,rolled,plate,Corresponding,area,fractions,increased,It,was,explained,by,thermodynamic,calculations,that,equilibrium,between,varied,temperature,Element,contents,decreased,solidification,cooling,Due,difference,rate,transformation,ratio,surface,center,also,affected,size,smaller,provided,better,kinetic,conditions,Critical,diameters,calculated,For,average,aspect,During,crushed,into,particles,phase,MgO,cores,leading
AB值：
0.437076
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。