Dynamic microstructure evolution and mechanical properties of dilute Mg-Al-Ca-Mn alloy during hot rolling
文献摘要：
The dynamic microstructure and texture of dilute Mg-0.50Al-0.71Ca-0.33Mn(wt.％)during hot rolling at two slab temperatures were investigated by electron backscattered diffraction(EBSD)and high resolu-tion transmission electron microscopy(HRTEM).The results show that the development of the rolling microstructures is to first form{10-12}extension twins in the original grains,thereby forming the extension-twinned regions,and then to further form{10-11}-{10-12}double twins and kinks in the extension-twinned regions,and finally to form continuous dynamic recrystallized(continuous DRXed)grains in the double twins and the cross parts of the shear-deformed coarse extension-twinned regions.These extension twins,double twins and kinks show a decisive effect on the formation of rolling texture.The number of{10-11}-{10-12}double twins and resultant the continuous DRX process are strongly affected by the rolling slab temperature and the reduction thickness per pass.By optimizing the rolling conditions,texture and microstructures of the multi-pass rolled Mg-Al-Ca-Mn alloy sheets are success-fully modified.Although the total alloy content is only 1.5 wt.％,these Mg-Al-Ca-Mn alloy sheets show much higher strength than the commercial Mg-3Al-1 Zn(wt.％)(AZ31B)sheet.
文献关键词：
中图分类号：
作者姓名：
Shiwei Xu;Congcong Zhu;Zhanhong Lin;Chen Jin;S.Kamado;K.Oh-ishi;Yun Qin
作者机构：
College of Materials Science and Engineering,Hunan University,Changsha 410082,China;State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body,Hunan University,Changsha 410082,China;Qinghai Salt Lake Teli Magnesium Co.Ltd.,Xining 810000,China;Department of Mechanical Engineering,Nagaoka University of Technology,Nagaoka 940-2188,Japan;Toyota Central R&D Labs.,Inc.,41-1 Yokomichi,Nagakute,Aichi 480-1192,Japan;Research Institute(R&D Centre),Baowu Steel Group Corporation,Shanghai 201900,China
文献出处：
引用格式：
[1]Shiwei Xu;Congcong Zhu;Zhanhong Lin;Chen Jin;S.Kamado;K.Oh-ishi;Yun Qin-.Dynamic microstructure evolution and mechanical properties of dilute Mg-Al-Ca-Mn alloy during hot rolling)[J].材料科学技术（英文版）,2022(34):1-14
A类：
50Al,71Ca,33Mn,kinks
B类：
Dynamic,evolution,mechanical,properties,dilute,Mg,alloy,during,hot,rolling,dynamic,texture,wt,two,slab,temperatures,were,investigated,electron,backscattered,diffraction,EBSD,resolu,transmission,microscopy,HRTEM,results,show,that,development,microstructures,first,extension,twins,original,grains,thereby,forming,twinned,regions,then,further,double,finally,continuous,recrystallized,DRXed,cross,parts,shear,deformed,coarse,These,decisive,effect,formation,number,resultant,process,are,strongly,affected,reduction,thickness,pass,By,optimizing,conditions,multi,rolled,sheets,success,fully,modified,Although,total,content,only,these,much,higher,strength,than,commercial,3Al,AZ31B
AB值：
0.463808
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。