Shear instability in heterogeneous nanolayered Cu/Zr composites
文献摘要:
Ultrastrong nanolayered metallic composites are usually subjected to low ductility due to plastic insta-bility during deformation.Here we investigated the shear instability of a newly designed heterogeneous nanolayered Cu/Zr composites by microindentation.The heterogeneity in size was generated by inserting a few thin Cu-Zr bilayers with an individual layer thickness of 2.5-10 nm into the interface region of the Cu/Zr layered composites with an individual layer thickness of 100 nm.The microindentation tests showed that multiple shear bands appeared in the heterogeneous composite with one bilayer,whereas only a single shear band was formed in that with two or three bilayers.Most importantly,the layer strain in the multi-shear band region is much smaller than that in the single-shear band area.For example,the strain of the 100 nm layers within the shear band in the composite with one 10 nm bilayer could reach as low as 2.8,which was less than half of that in the composite with three 10 nm bilayers,i.e.,6.1.These findings demonstrated that strain delocalization can be achieved through shear band multiplica-tion if an appropriate number of thin bilayers were used as interlayers in the 100 nm Cu/Zr composites.Besides,compared with the homogeneous composite with an individual layer thickness of 100 nm and the bimodal composite which is composed of alternating one 100 nm Cu-Zr bilayer and two 10 nm Cu-Zr bilayers,the heterogeneous composite with one bilayer displayed a higher strength(2.15 GPa)and a favorable resistance to strain localization.
文献关键词:
中图分类号:
作者姓名:
Jianjun Li;Feng Qin;Dingshun Yan;Wenjun Lu;Jiahao Yao
作者机构:
School of Mechanical and Electrical Engineering,Central South University,Changsha 410083,China;State Key Laboratory of High Performance Complex Manufacturing,Central South University,Changsha 410083,China;School of Materials Science and Engineering,Central South University,Changsha 410083,China;Department of Mechanical and Energy Engineering,Southern University of Science and Technology,Shenzhen 518055,China;Beijing Institute of Technology Chongqing Innovation Center,Chongqing 401120,China
文献出处:
引用格式:
[1]Jianjun Li;Feng Qin;Dingshun Yan;Wenjun Lu;Jiahao Yao-.Shear instability in heterogeneous nanolayered Cu/Zr composites)[J].材料科学技术(英文版),2022(10):81-91
A类:
nanolayered,Ultrastrong,microindentation,multiplica
B类:
Shear,instability,heterogeneous,Zr,composites,metallic,usually,subjected,low,ductility,due,plastic,during,deformation,Here,investigated,shear,newly,designed,by,heterogeneity,size,was,generated,inserting,few,bilayers,individual,thickness,into,interface,region,tests,showed,that,multiple,bands,appeared,one,whereas,only,single,formed,two,three,Most,importantly,strain,much,smaller,than,area,For,example,within,could,reach,which,less,half,These,findings,demonstrated,delocalization,can,achieved,through,if,appropriate,number,were,used,interlayers,Besides,compared,homogeneous,bimodal,composed,alternating,displayed,higher,strength,GPa,favorable,resistance
AB值:
0.385322
相似文献
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。