Microstructure and wear resistance of AlCrFeNiMo0.5Six high-entropy alloy coatings prepared by laser cladding
文献摘要：
In recent years, the coating prepared by laser cladding has attracted much attention in the field of wear research. In this work, AlCrFeNiMo0.5Six (x=0, 0.5, 1.0, 1.5, 2.0) high-entropy alloy coatings were designed and prepared on Q235 steel by laser cladding. The effect of Si content on microstructure, microhardness and wear resistance of the coatings was studied in detail. The results indicate that the AlCrFeNiMo0.5Six high-entropy alloy coatings show an excellent bonding between substrate and the cladding layer. The AlCrFeNiMo0.5Six coatings are composed of nano-precipitated phase with BCC structure and matrix with ordered B2 structure. With the addition of Si, the white phase (Cr, Mo)3Si with cubic structure appears in the interdendritic, and the morphology of the coating (x=2.0) transforms into lamellar eutectic-like structures. The addition of Si enhances the microhardness and significantly improves the wear resistance of the coatings. As x increases from 0 to 2.0, the average hardness of the cladding zone increases from 632 HV to 835 HV, and the wear rate decreases from 1.64×10-5 mm3·(N·m)-1 to 5.13×10-6 mm3·(N·m)-1. When x≥1.5, the decreasing trend of the wear rate gradually slows down. The wear rates of Si1.5 and Si2.0 coatings are 5.85×10-6 mm3·(N·m)-1 and 5.13×10-6 mm3·(N·m)-1, respectively, which is an order of magnitude lower than that of Q235 steel.
文献关键词：
中图分类号：
作者姓名：
Xiao-cong Li;Hui Liang;Yan-zhou Zhao;Li Gao;Li Jiang;Zhi-qiang Cao
作者机构：
Key Laboratory of Solidification Control and Digital Preparation Technology(Liaoning Province),School of Materials Science andEngineering,Dalian University of Technology,Dalian 116024,Liaoning,China;School of Physics and Electronic Technology,Liaoning Normal University,Dalian 116029,Liaoning,China
文献出处：
引用格式：
[1]Xiao-cong Li;Hui Liang;Yan-zhou Zhao;Li Gao;Li Jiang;Zhi-qiang Cao-.Microstructure and wear resistance of AlCrFeNiMo0.5Six high-entropy alloy coatings prepared by laser cladding)[J].中国铸造,2022(06):473-480
A类：
AlCrFeNiMo0,5Six
B类：
Microstructure,wear,resistance,high,entropy,alloy,coatings,prepared,by,laser,cladding,In,recent,years,attracted,much,attention,field,research,this,work,were,designed,Q235,steel,effect,content,microstructure,microhardness,was,studied,detail,results,indicate,that,show,excellent,bonding,between,substrate,layer,composed,nano,precipitated,phase,BCC,matrix,ordered,B2,With,addition,white,3Si,cubic,appears,interdendritic,morphology,transforms,into,lamellar,eutectic,like,structures,enhances,significantly,improves,increases,from,average,zone,HV,decreases,mm3,When,decreasing,trend,gradually,slows,down,rates,Si1,Si2,respectively,which,magnitude,lower,than
AB值：
0.453111
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。