Structure and magnetostriction of high Pr/Ce-content(Tb0.2Pr0.8)1-xCexFe1.93 Laves compounds
文献摘要：
The light rare earth Pr/Ce-contained(Tb0.2Pr0.8)1-xCexFe1.93(0≤x≤1.0)intermetallics were arc melted and magnetoelastic properties were investigated.The compounds of x≥0.40 are found to stabilize at ambient pressure in a single Laves phase with MgCu2-type C15 structure,which is attributed to the strong Ce 4f bonding.The mixed-valence behavior,with a support of the deviation from the linear Vegard's law for both lattice parameter a and saturation magnetization Ms,is observed at room tem-perature.The easy magnetization direction(EMD)was determined by the analysis of XRD on both magnetically aligned samples and the(440)splitting,that is,EMD lies toward<111>axis for x≤0.50 rotating to<110>for x=0.60,accompanied with the structural distortion from rhombohedral to orthorhombic.The substitution of Ce for Tb/Pr is conductive to the reduction of magnetocrystalline anisotropy,giving rise to an improvement of the low-field magnetostriction.The excellent magne-toelastic properties can be tailored by the Ce introduction,e.g.,the spontaneous magnetostriction co-efficient λ111 as large as 1150×10-6 for x=0.40,and the low-field induced magnetostriction achieving a high value of λa=180×10-6 at 80 kA/m for x=0.60.The excellent magnetoelastic properties and the combination in high Pr-content with low cost,suggest promising prospects in applications.
文献关键词：
中图分类号：
作者姓名：
Yihao Shen;Jinjun Liu;Qilin Ding;Mingkun Wang;Zhongbin Pan;Juan Du
作者机构：
Faculty of Materials Science and Chemical Engineering,Ningbo University,Ningbo 315211,China;Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,China
文献出处：
引用格式：
[1]Yihao Shen;Jinjun Liu;Qilin Ding;Mingkun Wang;Zhongbin Pan;Juan Du-.Structure and magnetostriction of high Pr/Ce-content(Tb0.2Pr0.8)1-xCexFe1.93 Laves compounds)[J].稀土学报（英文版）,2022(04):670-675
A类：
2Pr0,xCexFe1,magnetoelastic,MgCu2,magnetocrystalline,toelastic
B类：
Structure,magnetostriction,high,content,Tb0,Laves,compounds,light,rare,earth,contained,intermetallics,were,arc,melted,properties,investigated,found,stabilize,ambient,pressure,single,phase,type,C15,structure,which,attributed,strong,4f,bonding,mixed,valence,behavior,support,deviation,from,linear,Vegard,law,both,lattice,parameter,saturation,magnetization,Ms,observed,room,tem,perature,easy,direction,EMD,was,determined,by,analysis,magnetically,aligned,samples,splitting,that,lies,toward,axis,rotating,accompanied,structural,distortion,rhombohedral,orthorhombic,substitution,conductive,reduction,anisotropy,giving,rise,improvement,low,field,excellent,can,tailored,introduction,spontaneous,efficient,large,induced,achieving,value,kA,combination,cost,suggest,promising,prospects,applications
AB值：
0.536808
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。