Development of a hot-rolled 980 MPa advanced high-strength steel with excellent flangeability and bendability
文献摘要：
A new 980 MPa advanced high-strength steel(AHSS)with excellent bendability and flangeability has been studied and industrially produced,typical of tensile strength,fractured elongation,and hole expansion ratio(HER)exceeding 980 MPa,10％,and 30％,respectively.The 90° V-type bending perpendicular to the rolling direction can satisfy the R/t=1.0 requirement,indicating excellent bendability.Systematic evaluations of industrial trial-produced 980 MPa hot-rolled AHSS have been conducted,including microstructure,tensile properties in three directions,HER,bendability,fatigue limit strength,and forming limit.The microstructure of the newly developed 980 MPa AHSS primarily consists of fine bainite and a small amount of martensite-austenite constituent.The practical yield and tensile strength are higher than 800 and 980 MPa,respectively,with typical elongation of 13％and HER of around 40％.The good combination of the newly developed 980 MPa AHSS is primarily attributed to the fine bainitic microstructure,resulting in excellent flangeability and bendability.In addition,the newly developed 980 MPa AHSS has good fatigue and forming properties,making it suitable for the production of chassis and suspension components.
文献关键词：
中图分类号：
作者姓名：
ZHANG Chen;WANG Huanrong
作者机构：
Research Institute,Baoshan Iron&Steel Co.,Ltd.,Shanghai 201999,China
文献出处：
引用格式：
[1]ZHANG Chen;WANG Huanrong-.Development of a hot-rolled 980 MPa advanced high-strength steel with excellent flangeability and bendability)[J].宝钢技术研究（英文版）,2022(04):16-20
A类：
flangeability,bendability
B类：
Development,hot,rolled,advanced,strength,steel,excellent,AHSS,been,studied,industrially,produced,typical,tensile,fractured,elongation,hole,expansion,ratio,HER,exceeding,respectively,type,bending,perpendicular,rolling,can,satisfy,requirement,indicating,Systematic,evaluations,have,conducted,including,microstructure,properties,three,directions,fatigue,limit,forming,newly,developed,primarily,consists,fine,bainite,small,amount,martensite,austenite,constituent,practical,yield,are,higher,than,around,good,combination,attributed,bainitic,resulting,In,addition,making,suitable,production,chassis,suspension,components
AB值：
0.471569
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。