Bimetallic PtSn nanoparticles confined in hierarchical ZSM-5 for propane dehydrogenation
文献摘要:
A series of PtSn/hierarchical ZSM-5 catalysts were developed for propane dehydrogenation,in which the PtSn bimetallic particles are confined in the mesopores of hierarchical ZSM-5 zeolite.The synthesis of PtSn/hierarchical ZSM-5 catalysts was achieved via the loading of Pt and Sn species onto the hierarchical ZSM-5 catalysts that are obtained through a desilication of conventional ZSM-5.The PtSn/hierarchical ZSM-5 catalysts were fully characterized by XRD,N2 adsorption,STEM,XPS,and CO-IR techniques,which reveals that highly dispersed PtSn bimetallic nanoparticles are enclosed into mesopores of hierarchical ZSM-5.The catalytic performance of PtSn/hierarchical ZSM-5 is greatly affected by the concentrations of alkali solution in the desilication process and Sn/Pt ratios in PtSn bimetallic particles.The PtSn1.00/ZSM-5(0.8) catalyst shows the highest efficiency in propane dehydrogenation,which gives an initial con-version of 46% and selectivity of 98% at 570 ℃.The high efficiency in these PtSn/hierarchical ZSM-5 cat-alysts for propane dehydrogenation is mainly ascribed to the confinement of PtSn particles in the mesopores of hierarchical ZSM-5 zeolite.
文献关键词:
作者姓名:
Tianlei Wang;Zhikang Xu;Yuanyuan Yue;Tinghai Wang;Minggui Lin;Haibo Zhu
作者机构:
National Engineering Research Center of Chemical Fertilizer Catalyst,School of Chemical Engineering,Fuzhou University,Fuzhou 350002,China;State Key Laboratory of Coal Conversion,Institute of Coal Chemistry,Chinese Academy of Sciences,Taiyuan 030001,China;Qingyuan Innovation Laboratory,Quanzhou 362801,China
引用格式:
[1]Tianlei Wang;Zhikang Xu;Yuanyuan Yue;Tinghai Wang;Minggui Lin;Haibo Zhu-.Bimetallic PtSn nanoparticles confined in hierarchical ZSM-5 for propane dehydrogenation)[J].中国化学工程学报(英文版),2022(01):384-391
A类:
desilication,PtSn1
B类:
Bimetallic,nanoparticles,confined,hierarchical,ZSM,propane,dehydrogenation,series,catalysts,were,developed,which,bimetallic,are,mesopores,zeolite,synthesis,was,achieved,via,loading,species,onto,that,obtained,through,conventional,fully,characterized,by,N2,adsorption,STEM,XPS,techniques,reveals,highly,dispersed,enclosed,into,catalytic,performance,greatly,affected,concentrations,alkali,solution,process,ratios,shows,highest,efficiency,gives,initial,version,selectivity,these,mainly,ascribed,confinement
AB值:
0.353306
相似文献
Boosting molecular diffusion following the generalized Murray's Law by constructing hierarchical zeolites for maximized catalytic activity
Ming-Hui Sun;Shu-Shu Gao;Zhi-Yi Hu;Tarek Barakat;Zhan Liu;Shen Yu;Jia-Min Lyu;Yu Li;Shu-Tao Xu;Li-Hua Chen;Bao-Lian Su-State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology,Wuhan 430070,China;Laboratory of Inorganic Materials Chemistry(CMI),University of Namur,Namur B-5000,Belgium;Division of Analysis,Sinopec Beijing Research Institute of Chemical Industry,Beijing 100013,China;National Engineering Laboratory for Methanol to Olefins,Dalian National Laboratory for Clean Energy,Dalian Institute of Chemical Physics,Chinese Academy of Sciences,Dalian 116023,China;Nanostructure Research Centre,Wuhan University of Technology,Wuhan 430070,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。