Silicotungstic acid-derived WO3 composited with ZrO2 supported on SBA-15 as a highly efficient mesoporous solid acid catalyst for the alkenylation of p-xylene with phenylacetylene
文献摘要:
Highly dispersed silicotungstic acid-derived WO3 composited with ZrO2 supported on SBA-15(WZ/SBA-15)as an ordered mesoporous solid acid catalyst was prepared via a facile incipient wetness impregna-tion(IWI)method that active ingredients,ZrO2 and WO3,were impregnated into the channels of SBA-15 simultaneously with a subsequent calcination process.The relationship between catalyst nature and per-formance was explored by high resolution transmission electron microscopy(HRTEM),high-angle annu-lar dark-field scanning transmission electron microscopy(HAADF-STEM),FT-IR,X-ray photoelectron spec-troscopy(XPS),X-ray diffraction(XRD),N2 adsorption-desorption,NH3 temperature-programmed desorp-tion(NH3-TPD),and FT-IR of pyridine adsorption(Py-IR)characterization techniques.The catalytic perfor-mance of W12Z15/SBA-15 is not only greater than that of single component solid acid catalysts,WO3/SBA-15 and ZrO2/SBA-15,but also W12/Z15/SBA-15 prepared by impregnating active ingredients,ZrO2 and WO3,into SBA-15 in sequence.The outstanding performance of W12Z15/SBA-15 is derived from the strong in-teraction between ZrO2 and WO3,which results in more acid sites,and relatively high specific surface area,large pore volume,and ordered mesoporous structure of SBA-15.The characterization and reaction results clearly demonstrate that the synergy of ZrO2 and WO3 has a clear boost for the alkenylation.The optimized W12Z15/SBA-15-500 achieves a 99.4%conversion of phenylacetylene and a 92.3%selectivity of main product α-arylstyrene for the alkenylation of p-xylene with phenylacetylene,with very low level of oligomers producing at the same time.Moreover,W12Z15/SBA-15-500 shows excellent catalytic stability and regeneration.Therefore,W12Z15/SBA-15-500 is a promising solid acid catalyst for the alkenylation.
文献关键词:
作者姓名:
Xueting Bai;Yongle Guo;Zhongkui Zhao
作者机构:
State Key Laboratory of Fine Chemicals,Department of Catalysis Chemistry and Engineering,School of Chemical Engineering,Dalian University of Technology,Dalian 116024,China
引用格式:
[1]Xueting Bai;Yongle Guo;Zhongkui Zhao-.Silicotungstic acid-derived WO3 composited with ZrO2 supported on SBA-15 as a highly efficient mesoporous solid acid catalyst for the alkenylation of p-xylene with phenylacetylene)[J].中国化学快报(英文版),2022(03):1325-1330
A类:
Silicotungstic,alkenylation,phenylacetylene,silicotungstic,impregna,W12Z15,impregnating,arylstyrene
B类:
acid,derived,WO3,composited,ZrO2,supported,SBA,highly,efficient,mesoporous,solid,xylene,Highly,dispersed,WZ,ordered,was,prepared,via,facile,incipient,wetness,IWI,method,that,active,ingredients,were,impregnated,into,channels,simultaneously,subsequent,calcination,process,relationship,between,nature,explored,by,resolution,transmission,microscopy,HRTEM,angle,annu,dark,field,scanning,HAADF,STEM,FT,ray,photoelectron,troscopy,XPS,diffraction,N2,adsorption,desorption,NH3,temperature,programmed,TPD,pyridine,Py,characterization,techniques,catalytic,not,only,greater,than,single,component,catalysts,but,also,sequence,outstanding,performance,from,strong,teraction,which,results,more,sites,relatively,specific,surface,area,large,pore,volume,structure,reaction,clearly,demonstrate,synergy,has,boost,optimized,achieves,conversion,selectivity,main,product,very,low,level,oligomers,producing,same,Moreover,shows,excellent,stability,regeneration,Therefore,promising
AB值:
0.447477
相似文献
Regulating local charges of atomically dispersed Moδ+sites by nitrogen coordination on cobalt nanosheets to trigger water dissociation for boosted hydrogen evolution in alkaline media
Maoqi Cao;Kang Liu;Yao Song;Chao Ma;Yiyang Lin;Huangjingwei Li;Kejun Chen;Junwei Fu;Hongmei Li;Jun Luo;Yida Zhang;Xusheng Zheng;Junhua Hu;Min Liu-School of Chemistry and Chemical Engineering,Qiannan Normal University for Nationalities,Duyun 558000,Guizhou,China;State Key Laboratory of Powder Metallurgy,School of Physics and Electronics,Shenzhen Research Institute,School of Physical and Electronics,Central South University,Changsha 410083,Hunan,China;School of Materials Science and Engineering,Central South University of Forestry and Technology,Changsha 410004,Hunan,China;School of Materials Science and Engineering,Hunan University,Changsha 410082,Hunan,China;National Synchrotron Radiation Laboratory,University of Science and Technology of China,Hefei 230029,Anhui,China;School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450001,Henan,China
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。