Role of Microalloyed Y and Gd in Improving the Corrosion Resistance of Rolled Mg-3Al-1Zn Alloy
文献摘要：
The corrosion performances of rolled AZ31 alloy with addition of Y and Gd were comparatively investigated.The corrosion rates of AZ31 alloy modified with Y and Gd were 3.3 and 3.7 mm/y immersing for 24 h in 3.5 wt％NaCl solution,respec-tively,which were much lower than that of AZ31 alloy(23.6 mm/y).The remarkable improvement in corrosion performance by adding Y or Gd was ascribed to preferentially form less noble Al2Y or Al6GdMn6 and more protective corrosion product layer,resulting in the reduction in H2 evolution rate and the enhancement of passivity.
文献关键词：
中图分类号：
作者姓名：
Panpan Wang;Haitao Jiang;Yujiao Wang;Yun Zhang;Jingchao Tao
作者机构：
Shanghai Key Laboratory of Materials Laser Processing and Modification,and National Engineering Research Center of Light Alloy Net Forming,School of Materials Science and Engineering,Shanghai Jiao Tong University,Shanghai 200240,China;Institute of Engineering Technology,University of Science and Technology Beijing,Beijing 100083,China
文献出处：
引用格式：
[1]Panpan Wang;Haitao Jiang;Yujiao Wang;Yun Zhang;Jingchao Tao-.Role of Microalloyed Y and Gd in Improving the Corrosion Resistance of Rolled Mg-3Al-1Zn Alloy)[J].金属学报（英文版）,2022(06):941-947
A类：
Microalloyed,Al6GdMn6
B类：
Role,Improving,Corrosion,Resistance,Rolled,Mg,3Al,1Zn,Alloy,corrosion,performances,rolled,AZ31,addition,were,comparatively,investigated,rates,modified,immersing,wt,NaCl,solution,respec,which,much,lower,than,that,remarkable,improvement,by,adding,was,ascribed,preferentially,less,noble,Al2Y,more,protective,product,layer,resulting,reduction,H2,evolution,enhancement,passivity
AB值：
0.587162
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。