Microstructure and Mechanical Properties of AlSi10Mg Alloy Manufactured by Laser Powder Bed Fusion Under Nitrogen and Argon Atmosphere
文献摘要：
In order to study the effect of gas atmosphere on forming performance of laser powder bed fusion(LPBF),AlSi10Mg alloy was prepared by direct forming and in situ laser remelting under the shielding gas of argon and nitrogen in this study,and its microstructure and properties were characterized and tested,respectively.The results show that the forming performance of AlSi10Mg under nitrogen atmosphere is better than that of argon.Moreover,in situ laser remelting method can effectively enhance the relative density and mechanical properties of AlSi10Mg,in which the densification is increased to 99.5％.In terms of mechanical properties,after in situ remelting,ultimate tensile strength under argon protection increased from 444.85±8.73 to 489.45±3.20 MPa,and that under nitrogen protection increased from 459.21±13.77 to 500.14±5.15 MPa.In addition,the elongation is nearly doubled and the micro-Vickers hardness is increased by 20％.The research results provide a new regulation control method for the customization of AlSi10Mg properties fabricated by LPBF.
文献关键词：
中图分类号：
作者姓名：
Yunmian Xiao;Yongqiang Yang;Shibiao Wu;Jie Chen;Di Wang;Changhui Song
作者机构：
School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,China
文献出处：
引用格式：
[1]Yunmian Xiao;Yongqiang Yang;Shibiao Wu;Jie Chen;Di Wang;Changhui Song-.Microstructure and Mechanical Properties of AlSi10Mg Alloy Manufactured by Laser Powder Bed Fusion Under Nitrogen and Argon Atmosphere)[J].金属学报（英文版）,2022(03):486-500
A类：
B类：
Microstructure,Mechanical,Properties,AlSi10Mg,Alloy,Manufactured,by,Laser,Powder,Bed,Fusion,Under,Nitrogen,Argon,Atmosphere,In,order,study,gas,atmosphere,forming,performance,laser,powder,bed,fusion,LPBF,alloy,was,prepared,direct,situ,remelting,under,shielding,argon,nitrogen,this,its,microstructure,properties,were,characterized,tested,respectively,results,show,that,better,than,Moreover,method,can,effectively,enhance,relative,density,mechanical,which,densification,increased,terms,after,ultimate,tensile,strength,protection,from,addition,elongation,nearly,doubled,Vickers,hardness,research,provide,new,regulation,control,customization,fabricated
AB值：
0.571203
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。