Capillary electroosmosis properties of water lubricants with different electroosmotic additives under a steel-on-steel sliding interface
文献摘要：
The process of lubricant penetration into frictional interfaces has not been fully established,hence compromising their tribological performance.In this study,the penetration characteristics of deionized water(DI water)containing an electroosmotic suppressant(cetyltrimethylammonium bromide(CTAB))and an electroosmotic promoter(sodium lauriminodipropionate(SLI)),were investigated using steel-on-steel friction pairs.The results indicated that the lubricant with electroosmotic promoter reduced the coefficient of friction and wear scar diameter,whereas that with an electroosmotic suppressant exhibited an opposite behavior compared with DI water.The addition of SLI promoted the penetration of the DI water solution,thus resulting in the formation of a thick lubricating film of iron oxide at the sliding surface.This effectively reduced the abrasion damage,leading to a lower coefficient of friction and wear loss.
文献关键词：
中图分类号：
作者姓名：
Bohua FENG;Zhiqiang LUAN;Tao ZHANG;Jiawei LIU;Xiaodong HU;Jiju GUAN;Xuefeng XU
作者机构：
Key Laboratory of Special Purpose Equipment and Advanced Manufacturing Technology,Ministry of Education&Zhejiang Province,Zhejiang University of Technology,Hangzhou 310023,China;College of Mechanical Engineering,Changshu Institute of Technology,Changshu 215500,China
文献出处：
引用格式：
[1]Bohua FENG;Zhiqiang LUAN;Tao ZHANG;Jiawei LIU;Xiaodong HU;Jiju GUAN;Xuefeng XU-.Capillary electroosmosis properties of water lubricants with different electroosmotic additives under a steel-on-steel sliding interface)[J].摩擦（英文）,2022(07):1019-1034
A类：
electroosmosis,electroosmotic,lauriminodipropionate
B类：
Capillary,properties,water,lubricants,different,additives,under,steel,sliding,process,penetration,into,frictional,interfaces,has,not,been,fully,established,hence,compromising,their,tribological,performance,In,this,study,characteristics,deionized,DI,containing,suppressant,cetyltrimethylammonium,bromide,CTAB,promoter,sodium,SLI,were,investigated,using,pairs,results,indicated,that,reduced,coefficient,wear,scar,diameter,whereas,exhibited,opposite,behavior,compared,addition,promoted,solution,thus,resulting,formation,thick,lubricating,film,iron,oxide,surface,This,effectively,abrasion,damage,leading,lower,loss
AB值：
0.560519
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。