Cube texture evolution of N15W alloy substrates and La-Zr-O buffer layer of YBCO-coated conductors
文献摘要：
The cube texture evolution of Ni-5 at％W alloy deformed up to a very high strain was thoroughly investi-gated by X-ray diffraction(XRD)and electron back-scat-tered diffraction(EBSD)during the process of deformation,recrystallization and grain growth.A typical copper-type rolling texture,mainly consisting of compo-nents of S,copper and brass orientations,is obtained after heavy cold rolling.The fraction of rolling texture is slightly strengthened during recovery and then strongly reduced during recrystallization process.The cube texture is formed by consuming the rolling texture components during the discontinuous recrystallization process.The cube grains have a size advantage with respect to the non-cube grains.A strong cube-textured Ni5W alloy substrate with cube texture area fraction of 98.2％(＜10°)is obtained after annealing at 1050℃for l h.The full width half maximum(FWHM)values for the X-ray(111)ψ-scan and the(002)ω-scan of this substrate are 5.84° and 4.76°,respectively.Furthermore,the area fraction of{001}<110>orientation of the epitaxially grown La2Zr2O7 buffer layer is 97.1％(＜10°),and the FWHM values of(111)ψ-scan and(002)ω-scan are 5.22° and 5.00°,respectively.
文献关键词：
中图分类号：
作者姓名：
Pan Wang;Hui Tian;Hong-Li Suo;Cheng Ren;Ya-Ru Liang;Lin Ma;Min Liu
作者机构：
College of Materials Science and Engineering,University of Technology,Beijing 100124,China
文献出处：
引用格式：
[1]Pan Wang;Hui Tian;Hong-Li Suo;Cheng Ren;Ya-Ru Liang;Lin Ma;Min Liu-.Cube texture evolution of N15W alloy substrates and La-Zr-O buffer layer of YBCO-coated conductors)[J].稀有金属（英文版）,2022(11):3887-3894
A类：
N15W,Ni5W
B类：
Cube,evolution,alloy,substrates,buffer,layer,YBCO,coated,conductors,cube,deformed,up,high,strain,was,thoroughly,investi,gated,by,ray,diffraction,electron,back,scat,tered,EBSD,during,process,deformation,recrystallization,growth,typical,copper,type,rolling,mainly,consisting,brass,orientations,obtained,after,heavy,cold,slightly,strengthened,recovery,strongly,reduced,consuming,components,discontinuous,grains,have,size,advantage,textured,area,annealing,full,width,half,maximum,FWHM,values,scan,this,respectively,Furthermore,epitaxially,grown,La2Zr2O7
AB值：
0.458052
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。