Mechanical properties of Ti3AlC2 ceramics before and after heat treatment
文献摘要：
Ti3A1C2 ceramics were heat treated at the temperature from 1050 to 1450℃.Vickers hardness,fracture toughness,flexural strength and compressive strength of Ti3AlC2 were tested and calculated before and after heat treatment,respectively.Ti3AlC2 content,fracture toughness,flexural strength and compressive strength of Ti3AlC2 first increase and then decrease,while Vickers hardness is just the opposite with the increase in temper-ature from 1050 to 1450℃.After heat treatment at 1250℃,Ti3AlC2 content reaches the highest level of 94.2 wt％,and fracture toughness,flexural strength and compressive strength reach the maximum values,which are 6.4 MPa·m1/2,318 MPa and 662 MPa,respectively.Vickers hardness reduces to the lowest value of 2.9 GPa.Heat treatment does improve the strength and Ti3AlC2 content,but reduces the hardness and optimizes the mechanical properties of Ti3AlC2.
文献关键词：
中图分类号：
作者姓名：
Lei Yao;Chun-Cheng Zhu;Jiu-Xing Jiang;Bai-Bin Zhou
作者机构：
Key Laboratory of Design and Synthesis of Functional Materials and Green Catalysis,Harbin Normal University,Harbin 150025,China;College of Applied Sciences,Harbin University of Science and Technology,Harbin 150080,China
文献出处：
引用格式：
[1]Lei Yao;Chun-Cheng Zhu;Jiu-Xing Jiang;Bai-Bin Zhou-.Mechanical properties of Ti3AlC2 ceramics before and after heat treatment)[J].稀有金属（英文版）,2022(08):2777-2782
A类：
Ti3A1C2
B类：
Mechanical,properties,Ti3AlC2,ceramics,before,after,heat,treatment,were,treated,temperature,from,Vickers,hardness,fracture,toughness,flexural,strength,compressive,tested,calculated,respectively,content,first,increase,then,decrease,while,is,just,opposite,After,reaches,highest,level,wt,maximum,values,which,are,m1,reduces,lowest,GPa,Heat,does,improve,but,optimizes,mechanical
AB值：
0.415864
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。