Improving properties of fluxed iron ore pellets with high-silica by regulating liquid phase
文献摘要：
With rapid development of the pellet production under the background of green development,high-quality iron concen-trates were gradually exhausted;thus,using high-silica iron concentrates was expected to be a promising way to relieve resource pressure for pellet production.However,increasing the proportion of high-silica acid pellets into the furnace led to worse blast furnace slag,and the metallurgical properties of high-silica pellets were imperfect.To understand the reciprocal effects of basicity(CaO/SiO2)and MgO content on the properties of the high-silica pellets,the phase compositions and microstructure were investigated using X-ray diffraction and scanning electron microscope,equipped with energy dis-persive X-ray spectrometry.The results indicated that simply increasing MgO content from 0 to 2.50 wt.％ could decrease the reduction swelling index,but the compressive strength rapidly declined due to the formation of magnesioferrite.However,adding CaO to 2.50 wt.％ MgO pellets greatly improved the pellet qualities,which could be attributed to a substantial increase in the amount of high-melting-point silicate liquid phase.
文献关键词：
中图分类号：
作者姓名：
Yuan-bo Zhang;Xi-jun Chen;Zi-jian Su;Shuo Liu;Fang Chen;Nan-yong Wu;Tao Jiang
作者机构：
School of Minerals Processing and Bioengineering,Central South University,Changsha 410083,Hunan,China;Yangzhou Pacific Special Materials Co.,Ltd.,Yangzhou 225211,Jiangsu,China
文献出处：
引用格式：
[1]Yuan-bo Zhang;Xi-jun Chen;Zi-jian Su;Shuo Liu;Fang Chen;Nan-yong Wu;Tao Jiang-.Improving properties of fluxed iron ore pellets with high-silica by regulating liquid phase)[J].钢铁研究学报（英文版）,2022(09):1381-1392
A类：
fluxed,trates,magnesioferrite
B类：
Improving,properties,iron,ore,pellets,high,by,regulating,liquid,phase,With,development,production,background,green,quality,were,gradually,exhausted,thus,using,concentrates,was,expected,be,promising,way,relieve,resource,pressure,However,increasing,proportion,acid,into,furnace,led,worse,blast,slag,metallurgical,imperfect,To,understand,reciprocal,effects,basicity,CaO,SiO2,MgO,content,compositions,microstructure,investigated,ray,diffraction,scanning,electron,microscope,equipped,energy,dis,persive,spectrometry,results,indicated,that,simply,from,wt,could,decrease,reduction,swelling,compressive,strength,rapidly,declined,due,formation,adding,greatly,improved,qualities,which,attributed,substantial,increase,amount,melting,point,silicate
AB值：
0.573236
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。