Influence of pre-synthesized Al2O3-SiC composite powder from clay on properties of low-carbon MgO-C refractories
文献摘要：
To improve the properties of low-carbonization of MgO-C refractories,the introduction of composite additives is an effective strategy.Al2O3-SiC composite powder was prepared from clay using electromagnetic induction heating and carbon embedded methods.Further,the Al2O3-SiC composite powder synthesized by electromagnetic induction heating at 600 A was added into low-carbon MgO-C refractories(4 wt.％)to improve their properties.The results showed that when the addition amount of Al2O3-SiC composite powder is within the range of 2.5-5.0 wt.％,the properties of low-carbon MgO-C samples were significantly improved,e.g.,the apparent porosity of 7.58％-8.04％,the bulk density of 2.98-2.99 g cm-3,the cold compressive strength of 55.72-57.93 MPa,the residual strength after three air quenching at 1100℃of 74.86％-78.04％,and the decarburized layer depth after oxidized at 1400℃for 2 h of 14.03-14.87 mm.Consequently,the idea for the rapid synthesis of Al2O3-SiC composite powder provides an alternative low-carbon MgO-C refractories performance optimization strategy.
文献关键词：
中图分类号：
作者姓名：
Bei-yue Ma;Xin-ming Ren;Zhi Gao;Fan Qian;Zhao-yang Liu;Guo-qi Liu;Jing-kun Yu;Gao-feng Fu
作者机构：
Key Laboratory for Ecological Metallurgy of Multimetallic Mineral(Ministry of Education),Shenyang 110819,Liaoning,China;School of Metallurgy,Northeastern University,Shenyang 110819,Liaoning,China;State Key Laboratory of Advance Refractories,Sinosteel Luoyang Institute of Refractories Research Co.,Ltd.,Luoyang 471039,Henan,China
文献出处：
引用格式：
[1]Bei-yue Ma;Xin-ming Ren;Zhi Gao;Fan Qian;Zhao-yang Liu;Guo-qi Liu;Jing-kun Yu;Gao-feng Fu-.Influence of pre-synthesized Al2O3-SiC composite powder from clay on properties of low-carbon MgO-C refractories)[J].钢铁研究学报（英文版）,2022(07):1080-1088
A类：
refractories,decarburized
B类：
Influence,synthesized,Al2O3,SiC,composite,powder,from,clay,properties,low,MgO,To,carbonization,introduction,additives,effective,strategy,was,prepared,using,electromagnetic,induction,heating,embedded,methods,Further,by,added,into,wt,their,results,showed,that,when,addition,amount,within,range,samples,were,significantly,improved,apparent,porosity,bulk,density,cold,compressive,strength,residual,after,three,air,quenching,layer,depth,oxidized,Consequently,idea,rapid,synthesis,provides,alternative,performance,optimization
AB值：
0.46486
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。