Low cycle fatigue behavior of micro-grain casting K4169 superalloy at room temperature
文献摘要：
The strain-controlled low cycle fatigue tests were carried out at 298 K for the newly developed micro-grain casting K4169 superalloy,and the cyclic stress response,deformation and fracture behaviors of the alloy were studied.The results show that the fatigue life of the alloy was increased by more than two times compared with other casting K4169 alloys.This can be partly attributed to grain refinement impeding crack initiation and propagation.When the strain amplitude was in plastic range(Δεt/2≥0.5％),the alloy displayed a short period of initial cyclic stability followed by cyclic softening to fracture.By observing dislocation configurations,only a few dislocations moved around grain boundaries at initial cycles,leading to short cyclic stability.Afterwards,dislocations in the slip bands cut y"phase continuously leading to cyclic softening.When the strain amplitude was in elastic range(Δεt/2≤0.4％),the alloy exhibited elastic deformation and the peak stress kept stable.In addition,the crack initiation site changed from the MC carbides to the persistent slip bands on surface with increasing strain amplitudes.
文献关键词：
中图分类号：
作者姓名：
Rui Liu;Xitao Wang;Pinpin Hu;Chengbo Xiao;Jinshan He
作者机构：
Collaborative Innovation Center of Steel Technology,University of Science and Technology Beijing,Beijing,100083,China;Shandong Provincial Key Laboratory for High Strength Lightweight Metallic Materials,Advanced Materials Institute,Qilu University of Technology(Shandong Academy of Science),Jinan,250353,China;Science and Technology on Advanced High Temperature Structural Materials Laboratory,AECC Beijing Institute of Aeronautical Materials,Beijing,100095,China
文献出处：
引用格式：
[1]Rui Liu;Xitao Wang;Pinpin Hu;Chengbo Xiao;Jinshan He-.Low cycle fatigue behavior of micro-grain casting K4169 superalloy at room temperature)[J].自然科学进展·国际材料（英文）,2022(06):693-699
A类：
B类：
Low,fatigue,micro,grain,casting,K4169,superalloy,room,temperature,strain,controlled,tests,were,carried,out,newly,developed,cyclic,stress,response,deformation,fracture,behaviors,studied,results,show,that,life,was,increased,by,more,than,two,times,compared,other,alloys,This,can,partly,attributed,refinement,impeding,crack,initiation,propagation,When,plastic,range,displayed,short,period,initial,stability,followed,softening,By,observing,configurations,only,few,dislocations,moved,around,boundaries,cycles,leading,Afterwards,slip,bands,cut,phase,continuously,elastic,exhibited,peak,kept,stable,In,addition,site,changed,from,MC,carbides,persistent,surface,increasing,amplitudes
AB值：
0.5526
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。