Dual-enhancement of chromaticity and thermal stability:In-situ synthesis of core-shell γ-Ce2S3@CePO4 configuration
文献摘要：
Non-toxic rare earth(RE)composite materials are promising and active in optoelectronic fields,such as pigment.In this work,Na ions doped γ-Ce2S3 pigments were synthesized by solid-phase vulcanization and followed by in-situ synthesis to prepare an outer layer of CePO4 film.The characterizations of X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),solid state nuclear magnetic resonance(NMR)indicate that Na-dopedγ-Ce2S3 and CePO4 uniformly and tightly coated core-shell structure was successfully synthesized.The thermogravimetric analysis(TG)and reflection spectrum(RS)reveal that the CePO4 coating significantly improves the colorant and thermal stability performance of γ-Ce2S3.The excellent color quality of γ-Ce2S3@CePO4(L*=45.16,a*=55.94,b*=44.53)is achieved and the red color(L*=43.82,a*=49.79,b*=38.04)is still retained even if the sample is heated in air at 400℃for 30 min.
文献关键词：
中图分类号：
作者姓名：
Kanglong Hui;Wei Dong;Jipeng Fu;Mingxue Tang;Qi Wei;Chengyu Li;Hongjie Zhang
作者机构：
Changchun Institute of Applied Chemistry Chinese Academy of Sciences,Changchun 130022,China;Center for High Pressure Science and Technology Advanced Research,Beijing 100094,China;Institute of Optoelectronic Materials and Devices,China Jiliang University,Hangzhou 310018,China;College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China
文献出处：
引用格式：
[1]Kanglong Hui;Wei Dong;Jipeng Fu;Mingxue Tang;Qi Wei;Chengyu Li;Hongjie Zhang-.Dual-enhancement of chromaticity and thermal stability:In-situ synthesis of core-shell γ-Ce2S3@CePO4 configuration)[J].稀土学报（英文版）,2022(05):800-806
A类：
colorant
B类：
Dual,enhancement,chromaticity,thermal,stability,In,situ,synthesis,core,shell,Ce2S3,CePO4,configuration,Non,toxic,rare,earth,RE,composite,materials,promising,active,optoelectronic,fields,such,this,work,Na,doped,pigments,were,synthesized,by,solid,phase,vulcanization,followed,prepare,outer,layer,film,characterizations,ray,diffraction,scanning,microscopy,transmission,TEM,photoelectron,spectroscopy,XPS,state,nuclear,magnetic,resonance,NMR,indicate,that,uniformly,tightly,coated,structure,was,successfully,thermogravimetric,analysis,reflection,spectrum,RS,reveal,coating,significantly,improves,performance,excellent,quality,achieved,red,still,retained,even,sample,heated,air
AB值：
0.599423
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。