Conductive Polyacrylonitrile Fiber Prepared by Copper Plating with L-Ascorbic Acid as Reducing Agent
文献摘要：
Conductive polyacrylonitrile fibers were prepared by electroless copper plating under weak alkaline conditions, with L-ascorbic acid as reducing agent. The influences of CuSO4·5H2O, L-ascorbic acid, 2,2′-bipyridine and K4Fe(CN)6 concentration on the conductivity and mass gain percentage of the fibers were studied. The morphological structure of the fibers was characterized by scanning electron microscopy(SEM), and the mechanical properties of the fibers were analyzed through the mechanical property test. The results showed that the optimal reaction conditions were as follows: 26 g/L CuSO4·5H2O, 26 g/L L-ascorbic acid, 12 mg/L 2, 2′-bipyridine, 7 mg/L K4Fe(CN)6, and 38℃. The volume resistivity of the conductive PAN fibers prepared by the process was only 3.84×10-3 Ω·cm.
文献关键词：
中图分类号：
作者姓名：
WANG Yunhong;TAN Youzhi;XU Yajing;GUO Lamei;HUANG Liqian
作者机构：
Textile Inspection and Testing Institute,Jiangxi General Institute of Testing and Certification,Gongqing 332020,China;College of Textiles,Donghua University,Shanghai 201620,China;Key Laboratory of Textile Science&Technology,Ministry of Education,Donghua University,Shanghai 201620,China
文献出处：
引用格式：
[1]WANG Yunhong;TAN Youzhi;XU Yajing;GUO Lamei;HUANG Liqian-.Conductive Polyacrylonitrile Fiber Prepared by Copper Plating with L-Ascorbic Acid as Reducing Agent)[J].东华大学学报（英文版）,2022(06):519-526
A类：
Polyacrylonitrile
B类：
Conductive,Fiber,Prepared,by,Copper,Plating,Ascorbic,Acid,Reducing,Agent,polyacrylonitrile,fibers,were,prepared,electroless,copper,plating,under,weak,alkaline,conditions,ascorbic,acid,reducing,agent,influences,CuSO4,5H2O,bipyridine,K4Fe,CN,concentration,conductivity,mass,gain,percentage,studied,morphological,structure,was,characterized,scanning,electron,microscopy,mechanical,properties,analyzed,through,property,test,results,showed,that,optimal,reaction,follows,volume,resistivity,conductive,PAN,process,only
AB值：
0.608811
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。