Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys
文献摘要：
Evolution laws of microstructures, mechanical properties, and fractographs after different solution temperatures were investigated through various analysis methods. With the increasing solution temperatures, contents of the primary α phase decreased, and contents of trans-formed β structures increased. Lamellar α grains dominated the characteristics of transformed β structures, and widths of secondary α lamellas increased monotonously. For as-forged alloy, large silicides with equiaxed and rod-like morphologies, and nano-scale silicides were found. Si-licides with large sizes might be (Ti, Zr, Nb)5Si3 and (Ti, Zr, Nb)6Si3. Rod-like silicides with small sizes precipitated in retained β phase, exhib-iting near 45° angles with α/β boundaries. Retained β phases in as-heat treated alloys were incontinuous. 980STA exhibited an excellent com-bination of room temperature (RT) and 650℃ mechanical properties. Characteristics of fracture surfaces largely depended on the evolutions of microstructures. Meanwhile, silicides promoted the formation of mico-voids.
文献关键词：
中图分类号：
作者姓名：
Xiaozhao Ma;Zhilei Xiang;Tao Li;Yilan Chen;Yingying Liu;Ziyong Chen;Qun Shu
作者机构：
Faculty of Materials and Manufacturing,Beijing University of Technology,Beijing 100124,China;Pinggao Group CO.,LTD,State Grid Corporation of China,Pingdingshan 467000,China;Aviation Industry of China(AVIC)Manufacture technology institute,Beijing 100024,China
文献出处：
引用格式：
[1]Xiaozhao Ma;Zhilei Xiang;Tao Li;Yilan Chen;Yingying Liu;Ziyong Chen;Qun Shu-.Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys)[J].矿物冶金与材料学报,2022(08):1596-1607
A类：
fractographs,lamellas,silicides,licides,6Si3,Retained,incontinuous,980STA,mico
B类：
Evolution,laws,microstructures,mechanical,properties,during,heat,treatments,near,high,titanium,alloys,after,different,solution,temperatures,were,investigated,through,various,analysis,methods,With,increasing,contents,primary,decreased,increased,Lamellar,grains,dominated,characteristics,transformed,widths,secondary,monotonously,For,forged,equiaxed,rod,like,morphologies,nano,scale,found,sizes,might,be,Ti,Zr,Nb,5Si3,Rod,small,precipitated,retained,iting,angles,boundaries,phases,treated,exhibited,excellent,com,bination,room,Characteristics,fracture,surfaces,largely,depended,evolutions,Meanwhile,promoted,formation,voids
AB值：
0.523397
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。