Fabrication of green one-part geopolymer from silica-rich vanadium tailing via thermal activation and modification
文献摘要：
The aim of this investigation was to prepare geopolymeric precursor from vanadium tailing (VT) by thermal activation and modific-ation. For activation, a homogeneous blend of VT and sodium hydroxide was calcinated at an elevated temperature and then modified with metakaolin to produce a geopolymeric precursor. During the thermal activation, the VT was corroded by sodium hydroxide and then sodium silicate formed on the particle surfaces. After water was added, the sodium silicate coating dissolved to release silicon species, which created an alkaline solution environment. The metakaolin then dissolved in the alkaline environment to generate aluminum species, which was followed by geopolymerization. The VT particles were connected by a gel produced during geopolymerization, which yielded a geopolymer with excel-lent mechanical performance. This investigation not only improves the feasibility of using geopolymer technology for large-scale and in-situ applications, but also promotes the utilization of VT and other silica-rich solid wastes.
文献关键词：
中图分类号：
作者姓名：
Shenxu Bao;Yongpeng Luo;Yimin Zhang
作者机构：
Hubei Key Laboratory of Mineral Resources Processing and Environment,Wuhan University of Technology,Wuhan 430070,China;School of Resources and Environmental Engineering,Wuhan University of Technology,Wuhan 430070,China;State Environmental Protection Key Laboratory of Mineral Metallurgical Resources Utilization and Pollution Control,Wuhan University of Science and Techno-logy,Wuhan 430081,China;Hubei Collaborative Innovation Center for High Efficient Utilization of Vanadium Resources,Wuhan University of Science and Technology,Wuhan 430081,China
文献出处：
引用格式：
[1]Shenxu Bao;Yongpeng Luo;Yimin Zhang-.Fabrication of green one-part geopolymer from silica-rich vanadium tailing via thermal activation and modification)[J].矿物冶金与材料学报,2022(01):177-184
A类：
geopolymeric,modific
B类：
Fabrication,green,one,from,rich,vanadium,tailing,via,thermal,activation,modification,aim,this,investigation,prepare,precursor,VT,by,For,homogeneous,blend,sodium,hydroxide,calcinated,elevated,temperature,then,modified,metakaolin,During,corroded,silicate,formed,surfaces,After,water,added,coating,dissolved,release,silicon,species,which,created,alkaline,solution,environment,generate,aluminum,followed,geopolymerization,particles,were,connected,gel,produced,during,yielded,excel,lent,mechanical,performance,This,not,only,improves,feasibility,using,technology,large,scale,situ,applications,but,also,promotes,utilization,other,solid,wastes
AB值：
0.528644
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。